Comparison of the bond strength of laser-sintered and cast base metal dental alloys to porcelain |
| |
Authors: | Tolga Akova Yurdanur Ucar Alper Tukay Mehmet Cudi Balkaya William A Brantley |
| |
Affiliation: | Department of Prosthodontics, Faculty of Dentistry, Cukurova University 01330 Balcali, Adana, Turkey. |
| |
Abstract: | OBJECTIVE: The purpose of this study was to compare shear bond strengths of cast Ni-Cr and Co-Cr alloys and the laser-sintered Co-Cr alloy to dental porcelain. METHODS: Dental porcelain was applied on two cast and one laser-sintered base metal alloy. Ten specimens were prepared for each group for bond strength comparison. ANOVA followed by Tukey HSD multiple comparison test (alpha=0.05) was used for statistical analysis. Fractured specimens were observed with a stereomicroscope to classify the type of failure after shear bond testing. RESULTS: While the mean shear bond strength was highest for the cast Ni-Cr metal-ceramic specimens (81.6+/-14.6MPa), the bond strength was not significantly different (P>0.05) from that for the cast Co-Cr metal-ceramic specimens (72.9+/-14.3MPa) and the laser-sintered Co-Cr metal-ceramic specimens (67.0+/-14.9MPa). All metal-ceramic specimens prepared from cast Ni-Cr and Co-Cr alloys exhibit a mixed mode of cohesive and adhesive failure, whereas five of the metal-ceramic specimens prepared from the laser-sintered Co-Cr alloy exhibited the mixed failure mode and five specimens exhibited adhesive failure in the porcelain. CONCLUSIONS: The new laser-sintering technique for Co-Cr alloy appears promising for dental applications, but additional studies of properties of the laser-sintered alloy and fit of castings prepared by this new technique are needed before its acceptance into dental laboratory practice. SIGNIFICANCE: Laser sintering of Co-Cr alloy seems to be an alternative technique to conventional casting of dental alloys for porcelain fused to metal restorations. |
| |
Keywords: | Base metal alloys Laser-sintering Bond strength |
本文献已被 ScienceDirect 等数据库收录! |