Modelling of fatigue damage progression and life of CFRP laminates |
| |
Authors: | P PAPANIKOS K I TSERPES SP PANTELAKIS |
| |
Affiliation: | ISTRAM, Institute of Structures and Advanced Materials, Patron-Athinon 57, Patras 26441, Greece,;Laboratory of Technology and Strength of Materials, Department of Mechanical Engineering and Aeronautics, University of Patras, Patras 26500, Greece |
| |
Abstract: | A progressive fatigue damage model has been developed for predicting damage accumulation and life of carbon fibre‐reinforced plastics (CFRP) laminates with arbitrary geometry and stacking sequence subjected to constant amplitude cyclic loading. The model comprises the components of stress analysis, fatigue failure analysis and fatigue material property degradation. Stress analysis of the composite laminate was performed by creating a three‐dimensional finite element model in the ANSYS FE code. Fatigue failure analysis was performed by using a set of Hashin‐type failure criteria and the Ye‐delamination criterion. Two types of material property degradations on the basis of element stiffness and strength were applied: a sudden degradation because of sudden failure detected by the fatigue failure criteria and a gradual degradation because of the nature of cyclic loading, which is driven by the increased number of cycles. The gradual degradation of the composite material was modelled by using functions relating the residual stiffness and residual strength of the laminate to the number of cycles. All model components have been programmed in the ANSYS FE code in order to create a user‐friendly macro‐routine. The model has been applied in two different quasi‐isotropic CFRP laminates subjected to tension–compression (T–C) fatigue and the predictions of fatigue life and damage accumulation as a function of the number of cycles were compared with experimental data available in the literature. A very good agreement was obtained. |
| |
Keywords: | CFRP laminates composites fatigue finite element modelling life prediction progressive damage modeling |
|
|