CO2 solubility in dacitic melts equilibrated with H2O-CO2 fluids: Implications for modeling the solubility of CO2 in silicic melts

The solubility of CO₂ in dacitic melts equilibrated with H₂O-CO₂ fluids was experimentally investigated at 1250°C and 100 to 500 MPa. CO₂ is dissolved in dacitic glasses as molecular CO₂ and carbonate. The quantification of total CO₂ in the glasses by mid-infrared (MIR) spectroscopy is difficult because the weak carbonate bands at 1430 and 1530 cm⁻¹ can not be reliably separated from background features in the spectra. Furthermore, the ratio of CO_2,mol/carbonate in the quenched glasses strongly decreases with increasing water content. Due to the difficulties in quantifying CO₂ species concentrations from the MIR spectra we have measured total CO₂ contents of dacitic glasses by secondary ion mass spectrometry (SIMS).At all pressures, the dependence of CO₂ solubility in dacitic melts on x^fluid_CO2,total shows a strong positive deviation from linearity with almost constant CO₂ solubility at x_CO2fluid > 0.8 (maximum CO₂ solubility of 795 ± 41, 1376 ± 73 and 2949 ± 166 ppm at 100, 200 and 500 MPa, respectively), indicating that dissolved water strongly enhances the solubility of CO₂. A similar nonlinear variation of CO₂ solubility with x_CO2fluid has been observed for rhyolitic melts in which carbon dioxide is incorporated exclusively as molecular CO₂ (Tamic et al., 2001). We infer that water species in the melt do not only stabilize carbonate groups as has been suggested earlier but also CO₂ molecules.A thermodynamic model describing the dependence of the CO₂ solubility in hydrous rhyolitic and dacitic melts on T, P, f_CO2 and the mol fraction of water in the melt (x_water) has been developed. An exponential variation of the equilibrium constant K₁ with x_water is proposed to account for the nonlinear dependence of x_CO2,totalmelt on x_CO2fluid. The model reproduces the CO₂ solubility data for dacitic melts within ±14% relative and the data for rhyolitic melts within 10% relative in the pressure range 100-500 MPa (except for six outliers at low x_CO2fluid). Data obtained for rhyolitic melts at 75 MPa and 850°C show a stronger deviation from the model, suggesting a change in the solubility behavior of CO₂ at low pressures (a Henrian behavior of the CO₂ solubility is observed at low pressure and low H₂O concentrations in the melt). We recommend to use our model only in the pressure range 100-500 MPa and in the x_CO2fluid range 0.1-0.95. The thermodynamic modeling indicates that the partial molar volume of total CO₂ is much lower in rhyolitic melts (31.7 cm³/mol) than in dacitic melts (46.6 cm³/mol). The dissolution enthalpy for CO₂ in hydrous rhyolitic melts was found to be negligible. This result suggests that temperature is of minor importance for CO₂ solubility in silicic melts.