Preparation of TiB2 sintered compacts by hot pressing

A sintered compact of titanium diboride (TiB₂) was prepared by hot pressing of the synthesized TiB₂ powder, which was obtained by a solid-state reaction between TiN and amorphous boron. Densification of the sintered compact occurred at 20 MPa and 1800° C for 5 to 60 min with the aid of a reaction sintering, including the TiB₂ formation reaction between excess 20 at % amorphous boron in the as-synthesized powder (TiB₂ + 0.2B) and intentionally added 10 at % titanium metal. A homogeneous sintered compact of a single phase of TiB₂, which was prepared by hot pressing for 30 min from the starting powder composition (TiB₂ + 0.2B) + 0.1 Ti], had a fine-grained microstructure composed of TiB₂ grains with diameters of 2 to 3 m. The bulk density was 4.47 g cm^–3, i.e. 98% of the theoretical density. The microhardness, transverse rupture strength and fracture toughness of the TiB₂ sintered compact were 2850 kg mm^–2, 48 kg mm^–2 and 2.4 MN m^–3/2, respectively. The thermal expansion coefficient increased with increasing temperature up to 400° C and had a constant value of 8.8 x 10^–6 deg^–1 above 500° C.