Synthesis and characterization of degradable copoly(trans‐4‐hydroxy‐L‐proline/ϵ‐caprolactone)

The melt polycondensation reaction of N‐protected trans‐4‐hydroxy‐L ‐proline (N‐Z‐Hpr) and ?‐caprolactone (?‐CL) over a wide range of molar fractions in the feed produced new and degradable poly(N‐Z‐Hpr‐co‐?‐CL)s with stannous octoate as a catalyst. The optimal reaction conditions for the synthesis of the copolymers were obtained with 1.5 wt % stannous octoate at 140°C for 24 h. The synthesized copolymers were characterized by IR spectrophotometry, ¹H NMR, differential scanning calorimetry, and Ubbelohde viscometry. The values of the inherent viscosity (η_inh) and glass‐transition temperature (T_g) of the copolymers depended on the molar fractions of N‐Z‐Hpr. With an increase in the trans‐4‐hydroxy‐N‐benzyloxycarbonyl‐L ‐proline (N‐CBz‐Hpr) feed from 10 to 90 mol %, a decrease in η_inh from 2.47 to 1.05 dL/g, and an increase in T_g from ?48 to 49°C were observed. The in vitro degradation of these poly(N‐CBz‐Hpr‐co‐?‐CL)s was evaluated from weight‐loss measurements. © 2003 Wiley Periodicals, Inc. J Appl Polym Sci 88: 3176–3182, 2003