Microwave dielectric properties of SrLa[Ga1?x(Mg0.5Ti0.5)x]O4 and SrLa[Ga1?x(Zn0.5Ti0.5)x]O4 (x = 0.2-0.8) ceramics

SrLaGa_1?x(R_0.5Ti_0.5)_x]O₄ (R = Mg, Zn) ceramics were prepared by a standard solid state sintering method. The single-phase ceramics with K₂NiF₄-type layered perovskite structure and I4/mmm space group were obtained, indicating that SrLa(R_0.5Ti_0.5) and SrLaGaO₄ can form the unlimited solid solutions. With increasing x for R = Mg and Zn, ε_r increases monotonously, the Qf value first increases and then decreases, while τ_f increases from a negative to a positive value. The optimized microwave dielectric properties were obtained as following: ε_r = 23.3, Qf = 89 400 GHz, τ_f = ?0.8 ppm/°C for SrLaGa_0.6(Mg_0.5Ti_0.5)_0.4]O₄ and ε_r = 23.3, Qf = 76 200 GHz, τ_f = 0.2 ppm/°C for SrLaGa_0.7(Zn_0.5Ti_0.5)_0.3]O₄, indicating that the present solid solution ceramics are the promising candidates as microwave resonator materials for the telecommunication applications.