AZ91D镁合金屑的固相再生(英文)

利用固相再生技术回收利用AZ91D镁合金屑,具体工艺为先冷压再热挤。结果表明:制备的AZ91D镁合金具有较好的力学性能且晶粒明显细化。在热挤出过程中发生了动态再结晶,且动态再结晶组织受到热挤温度和应变速率的影响,在300-350 °C下基面滑移和孪晶协调变形导致动态再结晶晶粒产生,形成"项链"组织;在 350-400 °C下位错的交滑移控制动态再结晶形核;高于400 °C时位错攀移控制了整个动态再结晶过程,形成均匀的再结晶组织。随着应变速率增加AZ91D镁合金力学性能增大,改善了材料的力学性能,但应变速率过大,制备试样表面出现裂纹,影响材料的力学性能。

Solid-state recycling of AZ91D magnesium alloy chips

A method for recycling AZ91D magnesium alloy chips by solid-state recycling was studied. The experiments were carried out adopting the cold-press pressure and hot extrusion. The results indicate that recycled specimens of AZ91D magnesium alloy present better mechanical properties and consist of fine grains due to dynamic recrystallization. The mechanisms of dynamic recrystallization depend on plastic deformation process and change with the deformation temperature. At 300-350 °C, the deformation mechanisms are associated with the operation of basal slip and twinning, and the "necklace" structures are formed. At 350-400 °C, the cross slip results in the formation of new grains and grain refinement. At above 400 °C, the dynamic recrystallization mechanisms are controlled by dislocation climb, and recrystallized grains are homogeneous. The tensile strength of recycled specimens increases with the increase of the strain rate. When the strain rate is overhigh, the cracks and fractures in the surface appear and affect the tensile strength of recycled specimens.