Facile synthesis and characterization of rough surface $$\mathrm{V}_{2}\hbox {O}_{5}$$ nanomaterials for pseudo-supercapacitor electrode material with high capacitance

\(\hbox {V}_{2}\hbox {O}_{5}\) nanomaterials with rough surface were synthesized using commercial \(\hbox {V}_{2}\hbox {O}_{5}\), ethanol (EtOH) and \(\hbox {H}_{2}\hbox {O}\) as the starting materials by a simple hydrothermal route and combination of calcination. The electrochemical properties of \(\hbox {V}_{2}\hbox {O}_{5}\) nanomaterials as electrodes in a supercapacitor device were measured using cyclic voltammetry (CV) and galvanostatic charge–discharge (GCD) method. \(\hbox {V}_{2}\hbox {O}_{5}\) nanomaterials exhibit the specific capacitance of 423 F \(\hbox {g}^{-1}\) at the current density of 0.5 A \(\hbox {g}^{-1}\) and retain 327 F \(\hbox {g}^{-1}\) even at the high current density of 10 A \(\hbox {g}^{-1}\). The influence of the ratio of \(\hbox {EtOH/H}_{2}\hbox {O}\), the calcined time and temperature on the morphology, purity and electrochemical property of the products is discussed in detail. The results revealed that the ratio of \(\hbox {EtOH}\hbox {/}\hbox {H}_{2}\hbox {O}= 10\hbox {/}25\) and calcination at \(400{^{\circ }}\hbox {C}\) for 2–4 h are favourable for preparing \(\hbox {V}_{2}\hbox {O}_{5}\) nanomaterials and they exhibited the best electrochemical property. The novel morphology and high specific surface area are the main factors that contribute to high electrochemical performance of \(\hbox {V}_{2}\hbox {O}_{5}\) nanomaterials during the charge–discharge processes. It turns out that \(\hbox {V}_{2}\hbox {O}_{5}\) nanomaterials with rough surface is an ideal material for supercapacitor electrode in the present work.