Formation and properties of BaxFe3−xO4 with spinel structure by mechanochemical reaction of α-Fe2O3 and BaCO3

Magnetic Ba_xFe_3−xO₄ (x  0.23) with spinel structure was fabricated by ball milling of mixture of BaCO₃ and nonmagnetic α-Fe₂O₃ powders, and the molar ratio of BaCO₃ and α-Fe₂O₃ is 1:6. In the milling process, a mechanochemical reaction took place between BaCO₃ and α-Fe₂O₃, and Ba cation incorporated into α-Fe₂O₃ with rhombohedral structure to form a α-(Fe,Ba)₂O₃ solid solution. The Ba content in the α-(Fe,Ba)₂O₃ increased with increasing milling time, when the Ba content exceeded a limited solubility, the α-(Fe,Ba)₂O₃ transformed into a phase of Ba_xFe_3−xO₄ with spinel structure, where the Ba cation occupied an octahedral site or tetrahedral site. The product obtained in the balling process was different from that prepared in the annealing process at atmospheric pressure, which was BaFe₂O₄ with orthorhombic structure. Accompanying the crystal structure transition from α-(Fe,Ba)₂O₃ to Ba_xFe_3−xO₄, the magnetic properties also changed from nonmagnetism into ferromagnetism. The saturation magnetization was 53.3 emu/g and coercivity was 113.7 Oe. The mechanism of transitions of the crystal structure was discussed in the present work.