| Abstract: | Influence of thin oxide films on pitting corrosion of CrNi steels Chloride-induced pitting corrosion of stainless steel (Materials No. 1.4301 and 1.4571) was investigated with the aid of chronopotentiostatic tests. Oxide films upon the surface (temper colours), addition of inhibitors (sulphate and nitrate) and temperature were the testing variables. Two different critical pitting potentials have been found, which give information on the potential ranges for stable passivity, latent and stable pitting corrosion. The results only indicate a small effect of Mo content of the material and test temperature. The inhibitors (sulphate and nitrate) have a marked effect. Specimens with a clean surface produced by pickling are markedly more resistant against pitting corrosion than specimens with a yellow temper colour, whereas the difference in corrosion resistance between yellow and blue films is relatively small. The width of the critical potential range for pitting corrosion generally increases with increasing oxide film thickness. |