| 连铸大方坯生产H13工艺研究 |
| |
| 引用本文： | 马杰,陈林,陆明和.连铸大方坯生产H13工艺研究[J].宝钢技术,2013(6):16-19,24. |
| |
| 作者姓名： | 马杰 陈林 陆明和 |
| |
| 作者单位： | 宝山钢铁股份有限公司钢管条钢事业部,上海,201900;宝山钢铁股份有限公司研究院,上海,201900 |
| |
| 摘 要： | 采用电炉连铸大方坯新工艺生产的H13热作模具钢，通过与模铸工艺的H13钢相比较，研究新工艺对材料的成分和组织等方面的影响。结果表明，连铸大方坯生产的H13钢在成分控制、非金属夹杂物、显微硬度等方面都与模铸工艺接近，完全可以满足特定用途H13热作模具钢用户的需求。
|
| 关 键 词： | H13钢 轧制 大方坯 模铸 |
Research on the process of producing H13 steel via continuous bloom casting |
| |
| MA Jie,CHEN Lin and LU Minghe.Research on the process of producing H13 steel via continuous bloom casting[J].Baosteel Technology,2013(6):16-19,24. |
| |
| Authors: | MA Jie CHEN Lin and LU Minghe |
| |
| Affiliation: | 1. Tube, Pipe ＆ Bar Business Unit, Baoshan Iron ＆ Steel Co., Ltd., Shanghai 201900, China; 2. Research Institute, Baoshan Iron ＆ Steel Co. , Ltd. , Shanghai 201900, China) |
| |
| Abstract: | The new process of producing H13 hot-working die steel via continuous bloom casting was compared with the traditional process via mould casting. The influences of the new process on the composition and properties of steel were investigated. The results show that the HI5 steel produced via continuous bloom casting is equal to that produced via mould casting in chemical composition control, non-metallic inclusions and hardness, and can fully satisfy customer requirements on H13 hot-working die steel for special application. |
| |
| Keywords: | H13 steel rolling bloom mould casting |