New transparent conducting MgIn2O4---Zn2In2O5 thin films prepared by magnetron sputtering

New materials for a transparent conducting oxide film are demonstrated. Highly transparent Zn₂In₂O₅ films with a resistivity of 3.9 × 10^?4 Ω cm were prepared on substrates at room temperature using a pseudobinary compound powder target composed of ZnO (50 mol.%) and In₂O₃ (50 mol.%) by r.f. magnetron sputtering. MgIn₂O₄---Zn₂In₂O₅ films were prepared using MgIn₂O₄ targets with a ZnO content of 0–100 wt.%. The resistivity of the deposited films gradually decreased from 2 × 10^?3 to 3.9 × 10^?4 Ω cm as the Zn/(Mg + Zn) atomic ratio introduced into the films was increased. The greatest transparency was obtained in a MgIn₂O₄ film. The optical absorption edge of the films decreased as the Zn/(Mg + Zn) atomic ratio was increased, corresponding to the bandgap energy of their materials. It was found that the resistance of the undoped Zn₂In₂O₅ films was more stable than either the undoped MgIn₂O₄, ZnO or In₂O₃ films in oxidizing environments at high temperatures.