Crystal structures of Ni2SiO4 and Fe2SiO4 as a function of temperature and heating duration

X-ray structure refinements of Ni₂SiO₄ and Fe₂SiO₄ spinels have been made as a function of temperature and heating duration by intensity measurements at high temperatures and room pressure. The lattice parameters of Ni₂SiO₄ spinel linearly increased with temperature up to 1,000° C. However, Fe₂SiO₄ spinel exhibited a nonlinear thermal expansion and was converted to a polycrystalline mixture of spinel and olivine by heating of less than one-hour at 800° C. The ratios between the octahedral and tetrahedral bond lengths D _oct/D _tetr and between the shared and unshared edge distances (O-O)_sh/(O-O)_unsh in Fe₂SiO₄ spinel were both much larger than those in Ni₂SiO₄. These ratios increase with temperature. The Fe₂SiO₄ spinel more readily approached a activation state which facilitated the transition to the olivine structure than the Ni₂SiO₄ spinel. The lattice parameter of Ni₂SiO₄ spinel decreased with heating period at constant temperatures of 700° C and 800° C. The parameter of the quenched sample after heating for 52 h at 700° C was smaller than that of the nonheated sample. The refinements of the site occupancies at each heating duration indicated an increase in the cation deficiency in both tetrahedral and octahedral sites. Electron microprobe analysis, however, proved no significant difference in the chemical compositions between the quenched and nonheated samples. Si and Ni atoms displaced from normally occupied spinel lattice sites are assumed to settle in vacant sites defined by the cubic close packed oxygen sublattice in a manner which preserves the electric neutrality of the bulk crystal.