红外色谱分析二期高温高压处理Ceramage瓷聚体的单体转化率 |
| |
作者姓名: | 李 潇 杨 凯 赵 惠 金柱坤 |
| |
作者单位: | 解放军广州军区广州总医院口腔科,广东省广州市 510010 |
| |
基金项目: | 全军医学科技“十一五”计划(06Q034),“纳米二氧化硅填料牙科粘接剂的研制及其应用”;广州市科技计划项目(2007J1-D2021),以纳米二氧化硅为填料的牙科粘接剂的研制”。 |
| |
摘 要: | 背景:采用适当的方法提高材料的聚合程度,有利于改善其相应的理化性能。
目的:观察二期高温、高压处理对Ceramage瓷聚体单体转化率的影响。
方法:应用傅里叶变换红外色谱仪,分别测试经Solidilite聚合器固化的Ceramage体部材料和经过自控多用途树脂聚合仪在温度120 ℃,压力0.6 MPa,时间7 min条件下二次处理后的材料,在标准基线方法下得到各自的单体转化率并进行比较。
结果与结论:常规处理时Ceramage体部材料的单体转化率为(72.7±2.2)%,经二期热压处理后单体转化率为(75.4±1.5)%,提高幅度为2.7%。提示二期热压处理可以显著提高Ceramage体部材料的单体转化率,从而有可能改善材料的各项性能。
|
关 键 词: | 单体转化率 Ceramage瓷聚体 红外色谱 光固化 高温 高压 |
收稿时间: | 2011-03-29 |
Infrared spectra study of monomer conversion effect of post heated and press on Ceramage ceramic optimized polymer |
| |
Authors: | Li Xiao Yang Kai Zhao Hui Jin Zhu-kun |
| |
Affiliation: | Department of Stomatology, Guangzhou General Hospital of Guangzhou Military Command, Guangzhou 510010, Guangdong Province, China |
| |
Abstract: | BACKGROUND:Using appropriate methods to improve the degree of material polymerization will help to improve material physical and chemical properties.
OBJECTIVE:To study the influence of post heated and press on the monomer conversion of Ceramage ceramic optimized polymer material.
METHODS:Twenty Ceramage ceramic optimized polymer material specimens, with diameter of 4 mm and thickness of 3 mm, were double-side cured in Solidilite light cure case for 90 seconds. Ten random specimens had been post heated in 120 ℃ and pressured 0.6 MPa for 7 minutes by multi-purpose resign aggregator. The samples were crushed with a hydraulic machine. The monomer conversion of Ceramage ceramic optimized polymer material was obtained under different conditions.
RESULTS AND CONCLUSION:The monomer conversion of Ceramage ceramic optimized polymer material significantly increased from (72.7±2.2)% to (75.4±1.5)%, with the increasing degree of 2.7%. Post heated and press can significantly increase the monomer conversion of Ceramage ceramic optimized polymer material so as to improve material performance. |
| |