Crystallization of amorphous Ni60 Nb40?x Cr x alloys

Crystallization behaviour of amorphous Ni₆₀ Nb_40-x Cr _x (x = 0, 5, 10 and 13 at%) alloys was studied by differential Scanning calorimetry and X-ray diffraction measurements. It is shown that the addition of chromium reduces the crystallization temperature, stages of crystallization and activation energies associated with the crystallization sages of the Ni₆₀Nb₄₀ glass. Crystallization of the Ni₆₀Nb₄₀ glass occurred in three stages; in the initial stage a metastable M-phase formed in the amorphous matrix as reported earlier 1] . However, contrary to earlier observation 1], M -phase was not very stable and transformed together with some amorphous phase to the equilibrium Ni₃Nb phase in the second stage of crystallization. In the third stage, the remaining amorphous matrix transformed to the equilibrium NiNb phase. On addition of chromium the formation/stability of the M-phase was found to be suppressed and equilibrium NbCr₂ phase precipitated preferentially in the first stage. The second stage, corresponding to the formation of Ni₃Nb phase, remained almost unaltered. The third stage corresponding to the crystallization of NiNb phase disappeared completely at 13 at% Cr. In the fully crystallized samples the proportion of the NiNb phase decreased and that of NbCr₂ phase increased continuously with chromium concentration.