Oxide ionic conductivities of apatite-type lanthanum silicates and germanates and their possibilities as an electrolyte of lower temperature operating SOFC

Electrical properties of La_xM₆O_12+1.5x (M = Si, Ge) as an electrolyte for solid oxide fuel cell (SOFC) have been investigated. In La_xSi₆O_12+1.5x and La_xGe₆O_12+1.5x of x = 8–11, the highest conductivities were achieved at x = 9.7 (La_9.7Si₆O_26.55) and x = 9.0 (La_9.0(GeO₄)₆O_1.5), respectively. The conductivity of La_9.0(GeO₄)₆O_1.5 was higher than that of La_9.7Si₆O_26.55 in a temperature region higher than 700 °C, and the conductivity (2.4 × 10⁻³ S cm⁻¹) of La_9.7Si₆O_26.55 at 400 °C was higher than that (8.3 × 10⁻⁵ S cm⁻¹) of La_9.0(GeO₄)₆O_1.5. The power densities of SOFC (H₂ | Pt | electrolyte (thickness: 1 mm) | Pt | O₂) using La_9.0(GeO₄)₆O_1.5 as an electrolyte were 14.3 mW cm⁻² (700 °C) and 24.0 mW cm⁻² (800 °C). The corresponding SOFC using La_9.7Si₆O_26.55 was found to work even at lower temperatures of 400 and 500 °C with power densities of 0.011 and 0.12 mW cm⁻². The SOFC (H₂ | Ni–Sm_0.2Ce_0.8O_1.9 | electrolyte | Ba_0.5Sr_0.5Co_0.8Fe_0.2O_2.5 | air) using 0.3 mm thickness La_9.7Si₆O_26.55 electrolyte gave the 3.4 mW cm⁻² power density at 500 °C.