| 反应性阳离子水性聚氨酯对羊绒针织物抗起毛起球整理 |
| |
| 引用本文： | 陈建平,施伟利,李庆文,权衡. 反应性阳离子水性聚氨酯对羊绒针织物抗起毛起球整理[J]. 毛纺科技, 2012, 40(4): 31-34 |
| |
| 作者姓名： | 陈建平 施伟利 李庆文 权衡 |
| |
| 作者单位： | 1. 武汉纺织大学化学与化工学院,湖北武汉,430073
2. 武汉纺织大学纺织高分子研究所,湖北武汉,430073 |
| |
| 基金项目： | 中国纺织工业协会科技指导性项目(项目编号:2007049) |
| |
| 摘 要： | 以自制的阳离子型水性聚氨酯对纯羊绒针织物进行抗起毛起球整理,研究了整理剂应用工艺对纯羊绒针织物抗起毛起球整理效果的影响.研究结果表明:在整理剂最佳的应用工艺下(整理剂用量为80％ (owf)、工作液pH值5～6、处理浴温度40～50℃,20 min、热固工艺100℃烘干、110 ～120℃,5 min、浴比1∶25),助剂可显著提高羊绒针织物的抗起毛起球性能.其起毛起球等级可以提高2.0 ～2.5级,且织物的手感和白度等风格不受整理剂的影响.
|
| 关 键 词： | 反应性阳离子聚氨酯 羊绒 针织物 抗起毛起球 |
Pilling resistance of cashmere knitted fabrics with reactive cationic waterborne polyurethane |
| |
| CHEN Jian-ping , SHI Wei-li , LI Qing-wen , QUAN Heng. Pilling resistance of cashmere knitted fabrics with reactive cationic waterborne polyurethane[J]. Wool Textile Journal, 2012, 40(4): 31-34 |
| |
| Authors: | CHEN Jian-ping SHI Wei-li LI Qing-wen QUAN Heng |
| |
| Affiliation: | 1(1.College of Chemistry & Chemical Engineering,Wuhan Textile University,Wuhan 430073,China; 2.The Research Laboratory of High Polymer,Wuhan Textile University,Wuhan 430073,China) |
| |
| Abstract: | Pure cashmere knitted fabrics were treated for pilling resistance with reactive cationic waterborne polyurethane which was made by author ourselves.The paper studied the finishing effect of pure cashmere knitted fabrics with finishing agent and its application parameters.The results showed that the anti-pilling properties of cashmere knitted fabrics were improved markedly.The pilling resistance rate of which was raised 2.0 to 2.5 grades,and the handle and whiteness were not influenced by the finishing agent at the best parameters of finishing process(the mass concentration of finishing agent was 80%(owf),the pH value of finishing liquid was 5~6,then treated for 20 min at 40~50 ℃,thermosetting process was 100 ℃,110~120 ℃ for 5 min,the bath ratio was 1∶25) |
| |
| Keywords: | reactive cationic waterborne polyurethane cashmere knitted fabrics anti-pilling |