| 高温熔剂法制备硼酸铝晶须的研究 |
| |
| 引用本文： | 赵铭姝,翟玉春.高温熔剂法制备硼酸铝晶须的研究[J].材料科学与工艺,1998,6(3):81-83. |
| |
| 作者姓名： | 赵铭姝 翟玉春 |
| |
| 作者单位： | 东北大学材料与冶金学院 |
| |
| 摘 要： | 研究了高温熔剂法制行９Ａｌ２Ｏ３．２Ｂ２Ｏ３的方法，通过正交试验，利用方差和极并分析法对生长硼酸铝晶须的反应条件进行了优化，找出了生长硼酸铝晶须的最佳工艺条件。结果表明，在高温熔剂法制备肥的过程中，反应温度，氧化硼和氧化铝的摩尔配比及恒温时间为主要因素，并在最佳工艺条件下制得晶须的长经比５０～１００。
|
| 关 键 词： | 硼酸铝 晶须 高温熔剂法 制备工艺 陶瓷晶须 |
The Technique of Alumina Borate Whisker with High-Temperature Solvent Method |
| |
| Zhao Mingshu,Zhai Yuchun,Tian Yanwen.The Technique of Alumina Borate Whisker with High-Temperature Solvent Method[J].Materials Science and Technology,1998,6(3):81-83. |
| |
| Authors: | Zhao Mingshu Zhai Yuchun Tian Yanwen |
| |
| Abstract: | The manufacture of aluminum borate whisker by high-temperature solvent method was studied. The optimum technological condition of HTS was obtained through perpendicular experiments. The result was that the main factors influencing aluminum borate whisker were reaction temperature, molar ratio of B 2O 3 and Al(OH) 3, homothermal time. The productivity whisker whose lenth-radia was produced under the optimum technolocal condition. |
| |
| Keywords: | Alumium borate whiskers high temperature solvent technological condition |