Elevated-temperature tensile properties of irradiated 9 Cr-1 MoVNb steel

Normalized-and-tempered 9 Cr-1 MoVNb steel tensile specimens were irradiated in the Experimental Breeder Reactor-11 (EBR-11) at 390, 450, 500, and 550°C to ～2.1 and 2.5 × 10²⁶ neutrons/m² (> 0.1 MeV), which produced displacement damage levels of ～10 and 12 dpa, respectively. Tensile tests were conducted at the irradiation temperature and at room temperature. In addition to the irradiated specimens, as-heat-treated specimens and as-heat-treated specimens thermally aged at the irradiation for 5000 h were also tested.Thermal aging had no effect on the unirradiated tensile properties. Irradiation at 390°C increased the 0.2% yield stress and the ultimate tensile strength above those of the unirradiated control specimens. The ductility decreased slightly. After irradiation at 450, 500, and 550°C, the tensile properties were essentially the same as the unirradiated values. The hardening at 390°C was attributed to the dislocation and precipitate structure formed during the irradiation. The lack of hardening at 450°C and higher correlates with an absence of an irradiation-induced damage structure.