Characterization and properties of r.f.-sputtered thin films of the alumina–titania system

Thin films of the aluminum oxide (Al₂O₃)–titanium oxide (TiO₂) system including Al₂O₃, TiO₂, and Al₂O₃/TiO₂ were prepared by radio-frequency (r.f.) magnetron sputtering using ceramic targets of Al₂O₃, TiO₂, and Al₂O₃/TiO₂ composites with different Al₂O₃/TiO₂ ratio. These films were studied at different substrate temperatures, r.f. powers, and annealing temperatures. Composition, microstructure, thermomechanical property of internal stress, and mechanical property of scratch adhesion, were evaluated. A thin film with a dielectric constant of 62 and a loss tangent of 0.012 was obtained at 500 °C from a 10/90 target. This thin film remained the high dielectric constant of TiO₂, but had an improvement in the dielectric loss tangent. Al₂O₃-containing films had a higher resistivity and breakdown field, which was improved further by annealing. Optical properties, such as refractive index and optical transmittance, were also investigated.