Paederia foetida Linn. promoted synthesis of CoFe2 O4 and NiFe2 O4 nanostructures and their photocatalytic efficiency

A facile method of synthesis of cobalt ferrite (CoFe₂ O₄) and nickel ferrite (NiFe₂ O₄) nanoparticles (NPs) was developed using urea as a hydroxylating agent and Paederia foetida Linn. (family: Rubiaceae) leaf extract as a bio‐template. The synthesised ferrite NPs were characterised in a detailed manner by powder X‐ray diffraction (XRD), transmission electron microscopy, Fourier transform‐infrared spectroscopy and vibrating sample magnetometer analysis. The XRD patterns revealed the formation of cubic face‐centred phase for both CoFe₂ O₄ and NiFe₂ O₄ NPs. These quasi‐spherical particles of CoFe₂ O₄ and NiFe₂ O₄ were shown to have sizes in the range of 10–80 and 5–50 nm, respectively. The photocatalytic activity of metal ferrites was evaluated in H₂ O₂ assisted oxidative degradation of methylene blue (MB) and rhodamine B (RhB) under irradiation of solar light. Both metal ferrite photocatalysts exhibited pronounced activity in degradation of MB and RhB, respectively, but relatively higher activity was observed for NiFe₂ O₄. After completion, the catalysts were recovered using an external magnet. Recycling of these recovered catalysts up to five times showed no noticeable change in the efficiency.Inspec keywords: nanoparticles, nanofabrication, photochemistry, catalysts, cobalt compounds, nickel compounds, ferrites, X‐ray diffraction, transmission electron microscopy, Fourier transform infrared spectra, crystal structure, dyesOther keywords: Paederia foetida Linn, nanostructures, photocatalytic efficiency, cobalt ferrite nanoparticles, nickel ferrite nanoparticles, hydroxylating agent, leaf extract, bio‐template, powder X‐ray diffraction, transmission electron microscopy, Fourier transform‐infrared spectroscopy, vibrating sample magnetometer analysis, cubic face‐centred phase, quasi‐spherical particles, photocatalytic activity, methylene blue, rhodamine B, size 5 nm to 80 nm, CoFe₂ O₄ , NiFe₂ O₄