Co3O4/CeO2 composite oxides for methane emissions abatement: Relationship between Co3O4–CeO2 interaction and catalytic activity

Co₃O₄/CeO₂ composite oxides with different cobalt loading (5, 15, 30, 50, 70 wt.% as Co₃O₄) were prepared by co-precipitation method and investigated for the oxidation of methane under stoichiometric conditions. Pure oxides, Co₃O₄ and CeO₂ were used as reference. Characterization studies by X-ray diffraction (XRD), BET, temperature programmed reduction/oxidation (TPR/TPO) and X-ray photoelectron spectroscopy (XPS) were carried out.

An improvement of the catalytic activity and thermal stability of the composite oxides was observed with respect to pure Co₃O₄ in correspondence of Co₃O₄–CeO₂ containing 30% by weight of Co₃O₄. The combined effect of cobalt oxide and ceria, at this composition, strongly influences the morphological and redox properties of the composite oxides, by dispersing the Co₃O₄ phase and promoting the efficiency of the Co³⁺–Co²⁺ redox couple. The presence in the sample Co₃O₄(30 wt.%)–CeO₂ of a high relative amount of Ce³⁺/(Ce⁴⁺ + Ce³⁺) as detected by XPS confirms the enhanced oxygen mobility.

The catalysts stability under reaction conditions was investigated by XRD and XPS analysis of the used samples, paying particular attention to the Co₃O₄ phase decomposition. Methane oxidation tests were performed over fresh (as prepared) and thermal aged samples (after ageing at 750 °C for 7 h, in furnace). The resistance to water vapour poisoning was evaluated for pure Co₃O₄ and Co₃O₄(30 wt.%)–CeO₂, performing the tests in the presence of 5 vol.% H₂O. A methane oxidation test upon hydrothermal ageing (flowing at 600 °C for 16 h a mixture 5 vol.% H₂O + 5 vol.%O₂ in He) of the Co₃O₄(30 wt.%)–CeO₂ sample was also performed. All the results confirm the superiority of this composite oxide.