Valence-induced effects on the electrical properties of NiMn2O4 ceramics with different Ni sources

Spinel-structured NiMn₂O₄ ceramics, with different valence Ni sources, were originally prepared using Ni₂O₃ and NiO as raw materials, and the effects of different valence Ni sources on their electrical properties were first investigated. XRD patterns show that both Ni₂O₃-based and NiO-based NiMn₂O₄ ceramics are single cubic spinel structures. SEM/EDS images indicate that the NiMn₂O₄ ceramics exhibited high density at the experiment-determined sintering temperatures. XPS results and Raman drifts prove that the Ni valence-induced changes in Mn ions at B sites played a significant role in the electrical properties and thermal stability of NiMn₂O₄ ceramics. Compared with NiO-based NiMn₂O₄, the resistivity at 25°C (ρ_25°C) of Ni₂O₃-based NiMn₂O₄ increased dramatically from 3109 to 106958 Ω cm, the thermal constant (B_25/50) increased from 3264 to 4473 K, and the resistance shifts after annealing for 1000 h at 150°C decreased from 0.80% to 0.74%. The investigation of the relationship between the material properties and valence of Ni sources has provided a new and effective way for designing the spinel-structured negative temperature coefficient (NTC) materials by modulating the valence of ions at A sites in the raw materials.