Performance and characterization of Ru/Al2O3 and Ru/SiO2 catalysts modified with Mn for Fischer–Tropsch synthesis

Mn effect and characterization on γ-Al₂O₃-, -Al₂O₃- and SiO₂-supported Ru catalysts were investigated for Fischer–Tropsch synthesis under pressurized conditions. In the slurry phase Fischer–Tropsch reaction, γ-Al₂O₃ catalysts showed higher performance on CO conversion and C₅⁺ selectivity than -Al₂O₃ and SiO₂ catalysts. Moreover, Ru/Mn/γ-Al₂O₃ exhibited high resistance to catalyst deactivation and other catalysts were deactivated during the reaction. From characterization results on XRD, TPR, TEM, XPS and pore distribution, Ru particles were clearly observed over the catalysts, and γ-Al₂O₃ catalysts showed a moderate pore and particle size such as 8 nm, where -Al₂O₃ and SiO₂ showed highly dispersed ruthenium particles. The addition of Mn to γ-Al₂O₃ enhanced the removal of chloride from RuCl₃, which can lead to the formation of metallic Ru with moderate particle size, which would be an active site for Fischer–Tropsch reaction. Concomitantly, manganese chloride is formed. These schemes can be assigned to the stable nature of Ru/Mn/γ-Al₂O₃ catalyst.