Complex Effect of Sm3+/W6+ Codoping on α‐β Phase Transformation and Phonon Scattering of Oxygen‐Deficient La2Mo2O9

Lanthanum molybdate, La₂Mo₂O₉, has been attracted considerable attention owing to its high concentration of intrinsic oxygen vacancies, which could be reflected by enhanced phonon scattering and low thermal conductivity. A new series of La₂Mo₂O₉‐based oxides of the general formula La_2?xSm_xMo_2?xW_xO₉, where x ≤ 0.2, were synthesized by citric acid sol–gel process. The variation in thermal conductivity with Sm³⁺and W⁶⁺ fractions was analyzed based on structure information provided by X‐ray diffraction and Raman spectroscopy. The fully dense La_2?xSm_xMo_2?xW_xO₉ ceramics showed a minimum thermal conductivity value κ = 0.84 W·(m·K)^?1,T = 1073 K] at the composition of La_1.8Sm_0.2Mo_1.8W_0.2O₉, which stems from the multiple enhanced phonon scatterings due to mass and strain fluctuations at the La³⁺ and Mo⁶⁺ sites as well as the high concentration of intrinsic oxygen vacancies embedded in the crystal lattice. The thermal conductivities present an abrupt decrease at the structural transition, which is due to the phase transformation from a low‐temperature ordered form (monoclinic α‐La₂Mo₂O₉) to a high‐temperature disordered form (cubic β‐La₂Mo₂O₉₎.