Fabrication of Si3N4–SiC/SiO2 composites using 3D printing and infiltration processing

Si₃N₄–SiC/SiO₂ composites were prepared by employing three-dimensional (3D) printing using selective laser sintering (SLS) and infiltration processing. The process was based on the infiltration of silica sol into porous SLS parts, and silicon carbide and silicon nitride particles were bonded by melted nano-sized silica particles. To optimize the manufacturing process, the phase compositions, microstructures, porosities, and flexural strengths of the Si₃N₄–SiC/SiO₂ composites prepared at different heat-treatment temperatures and infiltration times were compared. Furthermore, the effects of the SiC mass fraction and the addition of Al₂O₃ and mullite fibers on the properties of the Si₃N₄–SiC/SiO₂ composites were investigated. After repeated infiltration and heat treatment, the flexural strength of the 3D-printed Si₃N₄–SiC/SiO₂ composite increased significantly to 76.48 MPa. Thus, a Si₃N₄–SiC/SiO₂ composite part with a complex structure was successfully manufactured by SLS and infiltration processes.