Preparation of Pt-PtOx thin films as electrode for memory capacitors

Pt-PtO_x thin films were prepared on Si(100) substrates at temperatures from 30 to 700°C by reactive r.f. magnetron sputtering with platinum target. Deposition atmosphere was varied with O₂/Ar flow ratio. The deposited films were characterized by X-ray diffraction, X-ray photoelectron spectroscopy and scanning electron microscopy. Resistively of the deposited films was measured by d.c. four probe method. The films mainly consisted of amorphous PtO and Pt₃O₄ (or Pt₂O₃) below 400°C, and amorphous Pt was increased in the film as a deposition temperature increased to 600°C. When deposition temperature was thoroughly increased, (111) oriented pure Pt films were formed at 700°C. Compounds included in the films strongly depended on substrate temperature rather than O₂/Ar flow ratio. Electrical resistivity of Pt-PtO_x films was measured to be from the order of 10^?1 Ω cm to 10^?5 Ω cm, which was related to the amount of Pt phase included in the deposited films.