New nanocomposite based on poly(lactic-co-glycolic acid) copolymer and magnetite. Synthesis and characterization |
| |
| Affiliation: | 1. Department of Applied Chemistry and Biochemistry, Kumamoto University, 2-39-1 Kurokami, Chuo-ku, Kumamoto 860-8555, Japan;2. Kumamoto Institute for Photo-Electro Organics, 3-11-38 Higashimachi, Higashi-ku, Kumamoto 862-0901, Japan;3. Department of Applied Chemistry and Chemical Engineering, Noakhali Science and Technology University, Sonapur, Noakhali 3814, Bangladesh;4. Department of New Frontier Science, Kumamoto University, 2-39-1 Kurokami, Chuo-ku, Kumamoto 860-8555, Japan;2. School of Life Science and Food Engineering, Huaiyin Institute of Technology, Huai''an, China.;3. Key Laboratory for Palygorskite Science and Applied Technology of Jiangsu Province, National & Local Joint Engineering Research Centre for Deep Utilization Technology of Rock-salt Resource, Faculty of Chemical Engineering, Huaiyin Institute of Technology, Huai''an, China. |
| |
| Abstract: | The study presents the preparation of the new magnetic nanocomposite based on PLGA and magnetite. The PLGA used to obtain the magnetic nanocomposites was synthesized by the copolymerization of lactic acid with glycolic acid, in the presence of tin octanoate Sn(Oct)2] as catalyst, by polycondensation procedure. Magnetite was obtained by co-precipitation from aqueous salt solutions FeCl2/FeCl3. The particles size of magnetite was 420 nm, and the saturation magnetization 62.78 emu/g, while the PLGA/magnetite nanocomposite size was 864 nm and the saturation magnetization 39.44 emu/g. The magnetic nanocomposites were characterized by FT-IR, DLS technique, SEM, VSM and simultaneous thermal analyses (TG–FTIR–MS). The polymer matrix PLGA acts as a shell and carrier for the active component, while magnetite is the component which makes targeting possible by external magnetic field manipulation. Based on the gases resulted by thermal degradation of PLGA copolymer, using the simultaneous analysis TG–FTIR–MS, a possible degradation mechanism was proposed. |
| |
| Keywords: | A: Polymer-matrix composites (PMCs) A: Nano-structures B: Magnetic properties D: Thermal analysis Evolved gases analysis |
| 本文献已被 ScienceDirect 等数据库收录！ |
|