| 加氢裂化装置管道腐蚀类型及材料的选用 |
| |
| 引用本文： | 张澄清.加氢裂化装置管道腐蚀类型及材料的选用[J].炼油技术与工程,2009,39(6):33-35. |
| |
| 作者姓名： | 张澄清 |
| |
| 作者单位： | 中国石化集团洛阳石油化工工程公司,河南省洛阳市,471003 |
| |
| 摘 要： | 介绍了加氢裂化装置中的主要腐蚀类型：高温氢损伤、高温H2＋H2S、高温硫腐蚀、湿H2S腐蚀、环烷酸腐蚀、NH4Cl及NH2HS腐蚀、连多硫酸腐蚀、胺应力腐蚀开裂以及装置中主要发生腐蚀的部位；分析了各种腐蚀发生的机理，提出了各腐蚀环境下管道材料的选用原则。
|
| 关 键 词： | 加氢裂化 腐蚀 管道材料 |
The corrosion forms in hydrocracking units and material selection |
| |
| Zhang Chengqing.The corrosion forms in hydrocracking units and material selection[J].Petroleum Refinery Engineering,2009,39(6):33-35. |
| |
| Authors: | Zhang Chengqing |
| |
| Affiliation: | Luoyang 471003;Henan;China |
| |
| Abstract: | The main corrosion forms in hydrocracking units are introduced,such as high-temperature hydrogen attack,high-temperature H2+H2S corrosion,high-temperature sulfur corrosion,wet H2S corrosion,naphthenic acid corrosion,NH4HS corrosion,polythionic acid corrosion,amine stress corrosion cracking as well as locations which are subject to corrosions in the unit.The corrosion mechanisms are analyzed,and material selection criteria for different corrosive environments are presented. |
| |
| Keywords: | hydrocracking corrosion piping material |