Extraction of nickel from ferromolybdenum leach residues

Abstract

The extraction of nickel from ferromolybdenum leach residues by sulphation roasting, water leaching and iron removal from subsequent nickel leach solutions was studied. Sulphation roasting and water leaching promote the reaction between sulphuric acid and the residue and decrease the silicon dissolution. Over 90% of Ni was leached. Ferric ions in the solution could be effectively removed as jarosite and ferric hydroxide. The recovery of nickel reached 88·3% under sulphation roasting with the sulphuric acid quality of 1472 kg t^?1 leach residue at 280°C for 4 h followed by iron removal with addition of 0·5 g NaClO₃, 6 g Na₂SO₄ and 10 g CaO/100 mL solution at 95°C for 2·5 h, while the concentration of iron in solution reduced to 0·38 from 56·6 g/L^?1.

On a étudié l’extraction du nickel à partir de résidu de lessivage de ferromolybdène par grillage sulfateur, lessivage à l’eau et enlèvement du fer des solutions obtenues de lessivage de nickel. Le grillage sulfateur et le lessivage à l’eau favorisent la réaction entre l’acide s ulfurique et le résidu et diminuent la dissolution de la silice. On a lessivé plus de 90% du Ni. On pouvait enlever efficacement de la solution les ions ferriques sous forme de jarosite et d’hydroxyde ferrique. La récupération du nickel atteignait 88·3% au moyen du grillage sulfateur, avec 1472 kg d’acide sulfurique par tonne de résidu de lessivage à 280°C pendant 4 h, suivi par l’enlèvement du fer avec l’addition de 0·5 g de NaClO₃, 6 g de Na₂SO₄ et 10 g de CaO par 100 mL de solution à 95°C pendant 2·5 h, la concentration du fer dans la solution étant réduite de 56·6 à 0·38 g L^?1.