Preparation and properties of nano-SiC strengthening Al2O3 composite ceramics |
| |
Authors: | Xiaolei ShiYali Dong Fumin Xu Yi TanLai Wang Jenn-ming Yang |
| |
Affiliation: | a School of Materials Science and Engineering, Dalian University of Technology, Linggong Road #2, Dalian 116024, China b Department of Materials Science and Engineering, University of California, Los Angeles, CA 90095, USA |
| |
Abstract: | The processing and mechanical behaviors of Al2O3-xwt.%SiC (x = 1, 2, 5, ASx) nano-composites prepared by the in situ synthesis of SiC from polycarbosilane (PCS) were investigated. The composites were densified by hot pressing. The microstructure and mechanical properties of the sintered composites were analyzed. The results showed that a fully dense structure was obtained when a few nano-SiC were doped and that the fracture toughness and strength were highly improved compared with those of monolithic Al2O3. The fracture toughness reached 5.1 MPa m1/2 in AS2 composite. The maximum flexural strength was 516 MPa obtained in AS1 composite. |
| |
Keywords: | Al2O3-SiC Polycarbosilane Flexural strength Fracture toughness |
本文献已被 ScienceDirect 等数据库收录! |
|