Effect of Nb2O5 on the microstructure and mechanical properties of TiAl based composites produced by hot pressing

In situ composites of TiAl reinforced with Al₂O₃ particles are successfully synthesized from an elemental powder mixture of Ti, Al and Nb₂O₅ by the hot-press-assisted reaction synthesis (HPRS) method. The as-prepared composites are mainly composed of TiAl, Al₂O₃, NbAl₃, as well as small amounts of the Ti₃Al phase. The in situ formed fine Al₂O₃ particles tend to disperse on the matrix grain boundaries of TiAl resulting in an excellent combination of matrix grain refinement and uniform Al₂O₃ distribution in the composites. The Rockwell hardness and densities of TiAl based composites increase gradually with increasing Nb₂O₅ content, and the flexural strength and fracture toughness of the composites have the maximum values of 634 MPa and 9.78 MPa m^1/2, respectively, when the Nb₂O₅ content reaches 6.62 wt.%. The strengthening mechanism was also discussed.