FERROFLUID CONTAINING SOLUBLE CONDUCTIVE POLYANILINE AND ITS FREESTANDING FILMS

Ferrofluid containing highly conductive polyaniline (PANI) was prepared, in which soluble PANI solutions dopedwith 10-camphorsulfonic acid (CSA) and dodecyl benzenesulfonic acid (DBSA) were used as the basic solution and Fe_3O_4nanoparticles (d = 10 nm) as the magnetic material. Moreover, the freestanding films of the resulting ferrofluid can beobtained by an evaporation method. The electrical and magnetic properties of the ferrofluid or its films can be adjustedthrough changing the content of PANI and Fe_3O_4. High saturated magnetization (≈ 30 emu/g) and high conductivity(≈ 250 S/cm) of the composite films can be achieved when the composite film contains 26.6 wt% of Fe_3O_4. In particular, itwas found that the composite films exhibit a super-paramagnetic behavior (Hc = 0) attributed to the size of Fe_3O_4 particles on the nanometer scale.

FERROFLUID CONTAINING SOLUBLE CONDUCTIVE POLYANILINE AND ITS FREESTANDING FILMS*

 Ferrofluid containing highly conductive polyaniline (PANI) was prepared, in which soluble PANI solutions dopedwith 10-camphorsulfonic acid (CSA) and dodecyl benzenesulfonic acid (DBSA) were used as the basic solution and Fe₃O₄nanoparticles (d = 10 nm) as the magnetic material. Moreover, the freestanding films of the resulting ferrofluid can beobtained by an evaporation method. The electrical and magnetic properties of the ferrofluid or its films can be adjusted through changing the content of PANI and Fe₃O₄.High saturated magnetization (≈ 30 emu/g) and high conductivity (≈250 S/cm) of thecomposite films can be achieved when the composite film contains 26.6 wt% of Fe₃O₄.In particular,it was found that the composite films exhibit a super-paramagnetic behavior(Hc=0)attributed to the size of Fe₃O₄ particles on the nanometer scale.