Siliconizing of molybdenum plate using Si2Cl6 and some of its properties

Molybdenum plate was siliconized using Si₂Cl₆ as a silicon source, and the siliconizing conditions and some of its properties were examined. The siliconizing of the molybdenum plate began by the deposition here and there of island-like MoSi₂ deposits 4 to 6m thick in the initial stage (after 10 min induction time), and then coalescence of the deposits proceeded to form a uniform MoSi₂ layer all over the molybdenum plate after 30 min siliconizing time. The weight decrease of the siliconized plate by anodic dissolution in 0.2 M sulphuric acid reduced exponentially with increasing thickness of the MOSi₂ layer, and no weight decrease was observed at all above 16m thickness. The sea water corrosion and sea sand abrasion resistivities of the siliconized molybdenum plate increased with increasing siliconizing temperature and Si₂Cl₆ flow rate.