Luminescent properties of red phosphors K2Ba(MoO4)2:Eu3+ for white light emitting diodes |
| |
作者姓名: | LI Zhaomei ZHONG Yingjuan GAOShaokang |
| |
作者单位: | College of Chemistry and Chemical Engineering, Fuzhou University, Fuzhou 350108, China |
| |
基金项目: | Foundation item: Project supported by Natural Science Foundation of Fujian Province (2011J033) |
| |
摘 要: | K2Ba(MoO4)2:Eu3+ phosphors were synthesized by solid-state reaction. The emission and excitation spectra of K2 Ba(MoO4)2:Eu3+ phosphors exhibited that the phosphors could be effectively excited by near ultraviolet (394 nm) and blue (465 nm) light, and emitted red light at 616 nm. The influence of Eu3+concentration, sintering temperature and charge compensators (K+, Na+ or Li+ ) on the emission intensity were investigated. The results indicated that concentration quenching of Eu3+ was not observed within 30mol.% Eu 3+, 600 oC was a suitable sintering temperature for preparation of K2 Ba(MoO4)2:Eu3+phosphors, and K+ ions gave the best improvement to enhance the emission intensity. The CIE chromaticity coordinates of K2 Ba(MoO4)2:0.05Eu3+phosphor were calculated to be (0.68, 0.32), and color purity was 97.4%.
|
关 键 词: | K2Ba(MoO4)2:Eu3+ red phosphor luminescence charge compensations rare earths |
收稿时间: | 13 February 2012 |
本文献已被 CNKI 维普 ScienceDirect 等数据库收录! |