Properties and mechanism of mullite whisker toughened ceramics

High-strength ceramics were prepared from high alumina fly ash (HAFA) and activated alumina as raw materials with magnesia as a sintering additive. The growth kinetics and influence mechanism of secondary mullite whiskers were investigated. Meanwhile, the effects of the Al₂O₃/SiO₂ mass ratio (A/S) and the amount of magnesia on the content and morphology of mullite in the green body were investigated, so as to emphasize the effect of the liquid phase in the sintering process on the growth of secondary mullite whiskers. The results showed that the aspect ratio of secondary mullite whiskers increased significantly after adding activated alumina to increase the A/S ratio of raw materials. When 30 wt% activated alumina was added, the mullite content increased by 5.39%, and the whisker length increased from 1.36 μm to 4.18 μm. The addition of magnesia improved the liquid phase formed during the sintering process and the K value method was used to determine the sintering liquid phase content under various conditions. It was observed that increasing the magnesia level by 1 wt% could raise the liquid phase content by 5–7%. When the total liquid content of the system was 30–40%, the growth activation energy in the diameter direction of the whisker reduced significantly, promoting the growth of secondary mullite whiskers along the C axis. The morphology of mullite gradually developed from fibrous to long columnar crystal, making it combine more densely with the green body matrix. Furthermore, the staggered long columnar mullite crystal structure changes the fracture mode of ceramics from intergranular to transgranular fracture, which fully uses the high mechanical strength of mullite. As a result, the fracture energy and strength of ceramics are significantly improved.