Macrostructures and mechanical properties of ultrasonic-assisted friction stir welding joint of 2024-T3 aluminium alloy

In friction stir welding of aluminum alloys, tunnel defect may occur due to insufficient plastic material flow caused by lower heat input in the weld region. The inadequacy in heat input is due to improper selection of friction stir welding tool and process parameters. Ultimately, such defects degrade the properties of weld and may pose serious concerns towards the integrity and safety of the weld component. In order to improve the properties of weld joints, an ultrasonic-assisted friction stir welding device has been configured where ultrasonic energy is transferred from an ultrasonic unit directly into one of the workpieces near the tool. Using this configuration, ultrasonic-assisted friction stir welding was conducted on 6 mm thick 2024-T3 aluminum alloy sheets. The macrostructure and mechanical properties of these welds were compared with the welds of this alloy prepared by conventional friction stir welding using identical process parameters. The results show that the welding speed can be increased while satisfactory weld quality is still ensured. The ultrasonic energy transferred in this configuration could enlarge the volume of weld nugget zone. Also, the influence of ultrasonic energy on the suppression or elimination of the tunnel defect is quite apparent. However, any beneficial effects of ultrasonic vibration on the tensile strength and the elongation of the joint were less obvious in this configuration.