Electrical characteristics of AlGaN/GaN HEMTs on 4-in diameter sapphire substrate |
| |
Authors: | Arulkumaran S Miyoshi M Egawa T Ishikawa H Jimbo T |
| |
Affiliation: | Res. Center for Nano-Device & Syst., Nagoya Inst. of Technol., Japan; |
| |
Abstract: | AlGaN/GaN high-electron-mobility transistors (HEMTs) were fabricated and the uniformity of dc properties were studied for the first time on 4-in diameter sapphire substrate. A quarter of 4-in diameter AlGaN/GaN epitaxial wafer was used for the uniformity studies of HEMTs. The observed average maximum drain current density, extrinsic transconductance and threshold voltage values for HEMTs were 515 mA/mm, 197 mS/mm, and -2.30 V with standard deviations 9.34%, 4.82%, and 6.52%, respectively. The uniformity of Hall mobility across the 4-in wafer was 1322 cm/sup 2//Vs with a standard deviation of 4.27%. The uniformity of sheet resistance across 4-in diameter wafer, measured using Hall Effect was 575 /spl Omega//sq. with a standard deviation 9.01%. The uniformity of HEMTs dc properties are in good correlation with the electrical characteristics of AlGaN/GaN heterostructures, which was obtained from the Hall Effect and capacitance-voltage (C-V) measurements. |
| |
Keywords: | |
|
|