Synthesis and properties of polyimides derived from cis- and trans-1,2,3,4-cyclohexanetetracarboxylic dianhydrides

Cis-1,2,3,4-cyclohexanetetracarboxylic dianhydride (cis-1,2,3,4-CHDA) was synthesized. It was found that under such conditions as heating or boiling in acetic anhydride, cis-1,2,3,4-CHDA could be converted to its trans-isomer. The process of thermal isomerization was monitored by ¹H NMR spectra and the mechanism of conversion was proposed. Their absolute structures of cis- and trans-1,2,3,4-CHDAs were elucidated by single crystal X-ray diffraction. The polycondensations of cis- and trans-1,2,3,4-CHDAs with aromatic diamines such as 4,4′-oxydianiline (ODA), 4,4′-methylenedianiline (MDA), 4,4′-diamino-3,3′-dimethyldiphenylmethane (DMMDA), 4,4′-bis(4-aminophenoxy)benzene (TPEQ), 2,2-bis4-(4-aminophenoxy)phenyl]propane (BAPP) were studied. It is easy to obtain higher molecular weight polyimides from trans-1,2,3,4-CHDA using conventional one-step or two-step methods. However, higher molecular weight polyimides derived from cis-1,2,3,4-CHDA could not be prepared by the usual methods (solid content ca. 10%) owing to the trend of forming cyclic oligomers. Increasing the concentration of monomers could give higher molecular weight cis-polymers. All of the cis-polyimides were soluble at room temperature in aprotic polar solvents and phenolic solvents and some of them even soluble in chloroform and tetrahydrofuran, while the corresponding trans-polymers showed poor solubility as compared to cis-polymers. All of the polyimides showed good thermal stability with the 5% weight loss temperatures in air over 415 °C. Furthermore, polyimides derived from cis-1,2,3,4-CHDA have higher glass transition temperatures (T_gs) than corresponding trans-polyimides. The flexible polyimide films possessed a tensile modulus range of 2.1-3.6 GPa, a tensile strength range of 42-116 MPa, an elongation at break of 4-18%. These polyimides exhibited cutoffs at wavelengths around 270 nm and were entirely colorless. All the polyimides showed amorphous pattern according to Wide angle X-ray diffraction measurements. The differences of polymerization and properties were explained by the structural changes resulted from isomerism.