| 摘 要： | Sr5LaTi3Nb7O30 ceramic was prepared by the conventional high temperature solid-state reaction route. The sintered samples were characterized by X-ray diffraction, scanning electron microscopy ( SEM ), differential thermal calorimetry ( DSC ) and dielectric measurements. The results show Sr5LaTi3Nb7O30 belongs to paraclectric phase of filled tetrngonal TB structure at room temperature, and undergoes a diffuse phase transition in the temperature range of -54-34℃ . And Sr5LaTi3Nb7O30 ceramic shows a high dielectric constant of 479 with a low dielectric loss of 0.005 at 1MHz . In comparison with Ba-based ceramics with TB structure, the temperature coefficients of the dielectric constant ( τt ) is significantly reduced.
|