Preparation of Pt/Ce–Zr–Y mixed oxide/anodized aluminium oxide catalysts for hydrogen passive autocatalytic recombination

The use of a Pt-based catalyst was evaluated for autocatalytic hydrogen recombination. The Pt was supported on a mixture of Ce-, Zr- and Y-oxides (CZY) to yield nanosized Pt particles. The Pt/CZY/AAO catalyst was then prepared by the spray-deposition of the Pt/CZY intermediate onto an anodized aluminium oxide (AAO) layer on a metallic aluminum core. The Pt/CZY/AAO catalyst (3 × 1 cm) was evaluated for hydrogen combustion (1–8 vol% hydrogen in the air) in a recombiner section testing station. The thermal distribution throughout the catalyst surface was investigated using an infrared camera. The maximum temperature gradient (ΔT) for the examined hydrogen concentrations did not exceed 36 °C. The Pt/CZY/AAO catalyst was also evaluated for prolonged hydrogen combustion duration to assess its durability. An average combustion temperature of 239.0 ± 10.0 °C was maintained for 53 days of catalytic hydrogen combustion, suggesting that there was limited, or no, catalyst deactivation. Finally, a Pt/CZY/AAO catalytic plate (14.0 × 4.5 cm) was prepared to investigate the thermal distribution. An average surface temperature of 212.5 °C and a maximum ΔT of 5.4 °C was obtained throughout the catalyst surface at a 3 vol% hydrogen concentration.     

Dual effect synergistically triggered Ce:(Y,Tb)3(Al,Mn)5O12 transparent ceramics enabling a high color-rendering index and excellent thermal stability for white LEDs

Ce:Y₃Al₅O₁₂ transparent ceramics (TCs) with appropriate emission light proportion and high thermal stability are significant to construct white light emitting diode devices with excellent chromaticity parameters. In this work, strategies of controlling crystal-field splitting around Ce³⁺ ion and doping orange-red emitting ion, were adopted to fabricate Ce:(Y,Tb)₃(Al,Mn)₅O₁₂ TCs via vacuum sintering technique. Notably, 85.4 % of the room-temperature luminescence intensity of the TC was retained at 150 °C, and the color rendering index was as high as 79.8. Furthermore, a 12 nm red shift and a 16.2 % increase of full width at half maximum were achieved owing to the synergistic effects of Tb³⁺ and Mn²⁺ ions. By combining TCs with a 460 nm blue chip, a warm white light with a low correlated color temperature of 4155 K was acquired. Meanwhile, the action mechanism of Tb³⁺ ion and the energy transfer between Ce³⁺ and Mn²⁺ ions were verified in prepared TCs.     

300M超高强钢在中性盐雾环境中的腐蚀行为及机制

摘要：为了研究300M超高强钢在中性盐雾环境中的腐蚀行为及腐蚀机制，采用失重法，宏观、微观腐蚀形貌分析，三维表面轮廓分析及电化学分析的研究方法，来表征腐蚀实验现象并进行分析。结果表明：300M超高强钢在中性盐雾环境中的腐蚀产物为FeOOH、Fe2O3、Fe(OH)3和Fe3O4；腐蚀速率随着腐蚀时间逐渐降低，腐蚀后期（72h）腐蚀速率降低50%；腐蚀初期以点蚀为主，点蚀坑通过横向扩展，逐渐发展为后期的均匀腐蚀，腐蚀表面形貌呈沟壑状；外腐蚀层对基体的保护能力很弱，Cr元素在锈层靠近基体的一侧偏聚使内腐蚀层具有一定的抗腐蚀性。     

基于(火用)效率目标的环冷机余热回收系统操作参数优化

摘要：针对烧结环冷机余热回收利用率不高的难题，采用分析法建立了评价某钢铁厂烧结环冷机余热回收系统运行效率的效率模型。基于多孔介质模型、局部非热平衡方程、真实气体SRK方程建立环冷机内气固两相换热模型。通过CFD仿真模拟，探究料层高度、循环风机输入烟气温度、烧结矿底部入口风速三项可控环冷机运行工艺参数对系统效率的影响规律。结果表明，料层厚度在1～1.5 m区间每增加0.1 m，效率增加0.8%～1.1%；循环风温在100～140℃之间每增加10℃，效率增加1.4%～1.5%；烧结矿底部入口风速在0.9～1.9 m/s之间每增加0.1 m/s，效率降低0.18%～0.24%。在此基础上，基于工业运行数据建立效率正交试验优化模型，提高了该余热回收系统3.42%的效率。     

离子液体水热法辅助合成稀土Ce掺杂ZnO纳米材料的制备及其应用研究

以1-甲基咪唑和氯代正丁烷为原料,合成1-丁基-3-甲基咪唑氯盐离子液体;以醋酸锌[Zn(Ac)2]、硫酸锌(ZnSO4)和氯化锌(ZnCl2)为锌源,在1-丁基-3-甲基咪唑氯盐离子液体和丙氨酸体系中与硝酸铈反应,经水热合成法制备得到Ce掺杂的纳米ZnO。采用扫描电子显微镜(SEM)、紫外-可见光吸收光谱(UV-Vis)、X射线衍射仪(XRD)、X射线光电子能谱分析(XPS)和红外光谱(FT-IR)对产品进行表征。以亚甲基蓝(MB)为目标降解物,采用UV-Vis检测,考察了Ce掺杂的纳米ZnO的光催化活性。研究表明,焙烧温度对光催化的晶体结构和光催化活性产生较大的影响;2%Ce/ZnO、焙烧温度为500℃、催化时间为30 min、亚甲基蓝用量0.05 g、pH值为10时降解率可达99.5%以上。     

03Cr18NiMoN节镍双相不锈钢的热变形行为及热加工图

关键词：双相不锈钢； 流变曲线； 本构方程； 热加工图     

DP980+Z烘烤硬化值与退火温度的关系

摘要：为了研究退火温度对镀锌DP980+Z烘烤硬化值的影响，退火温度控制在760～820℃之间，系统分析退火温度对烘烤硬化值的影响。通过准静态拉伸试验机测量烘烤硬化值及抗拉强度，采用lepara试剂对组织中的马氏体进行着色，利用金相显微镜及图像处理软件测量马氏体的体积分数；采用扫描电镜观察DP980+Z的双相组织特点，并且将组织图片通过CAD转化成有限元图进行网格划分，建立代表性体积单元（RVE），通过有限元分析铁素体、马氏体强度对烘烤硬化值的影响。在同样的变形量情况下，DP980+Z的原始屈服强度越高，烘烤硬化值越高。     

Unraveling the effect of alumina-supported Y- doped ceria composition and method of preparation on the WGS activity of gold catalysts

The demands for high-purity hydrogen required in fuel-cell applications impose new goals and challenges for design of well performing water-gas shift (WGS) catalysts. Gold-based catalysts have exhibited high activity in the WGS reaction at low temperature. Preparation of appropriate and economically viable supports with complex composition by various synthesis procedures is an attractive approach to WGS performance improvement. The effect of two different preparation methods (wet impregnation or mechanical mixing) and ceria content (10, 20 or 30 wt%) on textural, structural, surface and reductive properties and WGS activity of gold catalysts was studied. Additionally, the role of Y₂O₃ as a promoter of ceria was examined. Long-term stability test was carried out at 260 °C over the most active catalyst. The composition of the best performing sample (composed of about 70 wt% alumina), prepared by mechanical mixing, was considered promising in case of practical applications because of its cost efficiency. The combination of gold nanoparticles and alumina supported Y-doped ceria proved an advantageous approach for developing new catalytic formulations with high effectiveness in clean hydrogen production.     

In situ formation of multi scale reinforcing phases to improve performance of Al2O3-SiC C castables

In order to improve the physical properties and slag corrosion resistance of refractory materials for hot metal pretreatment, different contents of composite metal powders (CMP) were introduced into Al2O3-SiC-C refractory castables. The effect of CMP on the microstructure, physical properties and slag corrosion resistance of Al2O3-SiC-C refractory castables were studied. The results show that the multi scale reinforcing phases including flake crystals, rod shaped fibers, filamentous fibers and whiskers are in situ formed in the samples with addition of CMP, which result to the improvement of the cold modulus of rupture and cold crushing strength. When the addition of CMP is 6 wt.%, the high temperature modulus of rupture increases by 231%, the thermal shock resistance increases by 77% after thermal shock by water cooling 5 times and the percentage of the slag resistant area reduces by 37.2%.     

钾钠铌酸锶钡系列晶体自泵浦位相共轭镜的研究

报道了钾钠铌酸锶（ＫＮＳＢＮ）晶体系列自泵浦位相共轭反射镜的最新研究结果。ＫＮＳＢＮ：Ｃｕ、ＫＮＳＢＮ：Ｃｏ和ＫＮＳＢＮ：Ｃｅ自泵浦位相共轭反射镜的反射率分别可达７３％、７３％和８４．３％，ＫＮＳＢＮ：Ｃｕ自泵浦位相共轭反射镜的响应时间在低功率下达２００ｍｓ。