Mechanical properties,corrosion resistance,and rubber pad forming of cold differential speed-rolled pure titanium for bipolar plates of proton-exchange membrane fuel cells

Due to problems such as pores on surface-treated coatings, the corrosion resistance of pure titanium bipolar plates for proton-exchange membrane fuel cells can be further improved by increasing the corrosion resistance of pure titanium by using differential speed-rolling (DSR); however, these materials have not yet reached the standard requirements of bipolar plates (corrosion current density i_corr＜10³ nA·cm^?2). In this work, the corrosion resistance of pure titanium was improved by optimizing the DSR process while the strength was maintained. The best corrosion resistance of the DSR pure titanium was achieved when the roller speed ratio was 2, while i_corr was 429 nA·cm^?2 in a solution of 0.5 M H₂SO₄ and 2 mg/L HF at room temperature. The formability of the DSR pure titanium for bipolar plates was verified. The optimal holding pressure range was 6.8–7.0 kN.     

Unipolar plasma electrolytic oxidation: Waveform optimisation for corrosion resistance of commercially pure titanium

This study deals with the anodisation of titanium grade 2 in 0.5-M sulphuric acid using a pulsed signal in a unipolar regime. The electrical parameters investigated are voltage, frequency and duty cycle. The use of duty cycles with a high percentage of anodic polarisation (90%), combined with high frequencies (1000 Hz) and the higher voltage tested (220 V), favoured the establishment of a plasma regime involving strong dielectric discharges, allowing the growth of thicker oxides but with rough architecture. The corrosion resistance of the formed film has been characterised by potentiodynamic tests in 0.5-M NaBr for localised corrosion resistance and by immersion tests in 10% v/v sulphuric acid solution for a uniform corrosion assessment. Current–time curves, visual observations and electron microscope analysis (scanning electron microscopy, energy-dispersive X-ray spectroscopy) were the tools selected to provide a correlation between technological parameters and oxide growth mechanism. For localised and uniform corrosion, anodisation at 220 V with a high level of anodic polarisation (90%) and frequency (1000 Hz) was verified to be particularly advantageous.     

Surface treatment of titanium dioxide nanopowder using rotary electrode dielectric barrier discharge reactor

Titanium dioxide (TiO2) nanopowder (P-25;Degussa AG) was treated using dielectric barrier discharge (DBD) in a rotary electrode DBD (RE-DBD) reactor.Its electrical and optical characteristics were investigated during RE-DBD generation.The treated TiO2 nanopowder properties and structures were analyzed using x-ray diffraction (XRD) and Fourier-transform infrared spectroscopy (FTIR).After RE-DBD treatment,XRD measurements indicated that the anatase peak theta positions shifted from 25.3° to 25.1°,which can be attributed to the substitution of new functional groups in the TiO2 lattice.The FTIR results show that hydroxyl groups (OH) at 3400 cm-1 increased considerably.The mechanism used to modify the TiO2 nanopowder surface by air DBD treatment was confirmed from optical emission spectrum measurements.Reactive species,such as OH radical,ozone and atomic oxygen can play key roles in hydroxyl formation on the TiO2 nanopowder surface.     

高强WSTi544221合金组织与性能研究

研究了轧制变形量对WSTi544221合金棒材显微组织和力学性能的影响,并对Φ10 mm规格的棒材进行不同制度的固溶+时效处理,对比了不同热处理状态下棒材的组织和力学性能。结果表明,随着轧制变形量的增大,WSTi544221合金棒材的晶粒细化程度增大,强度逐渐提高,但塑性变化不大。经870℃×1 h/WC+520℃×6 h/AC固溶+时效处理后,强度与塑性可以获得良好匹配,当抗拉强度达到1 610 MPa、屈服强度达到1 531 MPa时,延伸率和断面收缩率可分别保持在12%和43%。     

钛合金表面多磁极耦合旋转磁场光整加工特性

面向激光增材制造钛合金表面的光整加工需求，设计出一种多磁极耦合旋转磁场光整加工装置来研究光整加工特性。基于ANSYS Maxwell仿真软件分析了光整加工装置的磁场强度分布。搭建了实验光整平台，分析了主轴转速、C轴转速和加工间隙对表面质量的影响。结果表明，在主轴转速500 r/min、C轴转速160 r/min和加工间隙0.7 mm的加工条件下，表面粗糙度Ra由5.991 μm下降至0793 μm。扫描电子显微镜(SEM)观测表明，光整后的钛合金表面沉积层消失，表面质量得到显著改善。     

工艺参数对超声辅助脉冲电沉积镍-氮化钛复合镀层的影响

在45钢表面以超声波辅助脉冲电沉积制备Ni-TiN复合镀层。研究了平均阴极电流密度、脉冲占空比、超声功率和TiN粒子(平均直径20~30 nm)添加量对复合镀层的TiN粒子含量和显微硬度的影响。得到较优的工艺参数为:NiSO4ꞏ6H2O 300 g/L,NiCl2ꞏ6H2O 30 g/L,H3BO330 g/L,十二烷基硫酸钠0.3 g/L,TiN 25 g/L,pH 4.1~4.3,温度40°C,平均阴极电流密度4 A/dm2,脉冲占空比40%,脉冲频率1000 Hz,超声功率300 W,机械搅拌速率200 r/min,时间60 min。该条件下所得Ni-TiN复合镀层的TiN质量分数为8.35%,显微硬度为819 HV,表面平整、致密,晶粒尺寸均匀。     

铸态Ti-20Zr-20Al钛合金动态压缩力学性能与断裂机制研究

采用X射线衍射仪、金相显微镜、分离式霍普金森杆和扫描电镜等手段研究了Ti-20Zr-20Al钛合金在动态压缩条件下的微观结构、力学性能和断裂机制。结果表明,Ti-20Zr-20Al铸态合金由Zr基体相和TiAl/Ti₃Al针状相组成; 随着应变率增加,合金的抗压强度增加,失效应变显著增加; Ti-20Zr-20Al合金的断裂机制为解理断裂; 随着应变率增加,试验压缩断裂后碎片总数增大,平均粒径减小。采用DID模型模拟的材料碎片尺度与实验结果比较吻合,Grady模型与实验结果的偏差较大。     

一种钛白粉转窑煅烧尾气余热利用新装置

钛白粉煅烧转窑尾气的高湿、高硫、高酸露点的特性使得转窑尾气余热利用过程中换热器寿命不理想。在总结已有尾气余热利用方式存在问题的基础上,提出了一种长寿命、易维护的套管式热管余热利用装置,该装置由彼此分离的换热套管通过弯头、法兰连接成为整体,尾气垂直横掠双层套管段,与高硫、高湿的尾气通过相变介质的相变完成热量由尾气向取热介质的转移,产生钛白粉生产工艺所急需的蒸汽,双层管的相变换热套管对比单层管的重力热管换热器寿命明显延长;连接换热套管的单层管弯头不与高湿、高硫尾气换热,大大减轻了尾气对单层管的腐蚀。换热器应用在3.6 m×58 m的钛白粉煅烧窑上,每年可以产生0.9 MPa的水蒸气1.12万t,为企业带来可观的经济效益。