Transparent and flexible films of new segmented polyurethane nanocomposites incorporated by NH2-functionalized TiO2 nanoparticles

In this work, TiO₂ nanoparticles are surface modified by NH₂-terminated organic moieties arised from 4,4′-methylene diphenyl diisocyanate (MDI). These nanoparticles are incorporated into ether-based segmented polyurethane (SPU) matrix. MDI is utilized as monomer together with poly(tetramethylene oxide) (PTMO) comonomer for preparing the final polymer as well. The NH₂-functionalized TiO₂ nanoparticles are covalently linked to the NCO terminals of the resulting SPU macromolecules during film preparation stage. Therefore, in addition to butylene glycol, these surface modified nanoparticles with enhanced organophilicity could play the role of the second chain extender of NCO-capped SPU macromolecules through formation of urea linkages. Optical and thermal behaviors of the transparent and flexible film (SPU/TiO₂–MDI) is compared with those of unmodified TiO₂ (SPU/TiO₂) and TiO₂-unloaded SPU films. Though the particle loading is only 5 wt.%, incorporation of TiO₂ and TiO₂–MDI nanoparticles into the SPU polymer enhances significantly the light absorption in UV region at 300–400 nm. SEM images of the prepared films clearly show a considerable decrease in particle aggregation for TiO₂–MDI into SPU matrix compared to that of unmodified TiO₂. TG analyses indicate a one-step decomposition pattern with onset temperatures of about 360 and 380 °C for neat SPU and SPU/TiO₂–MDI, respectively. Moreover, DTA thermograms of both nanocomposites show obviously two exothermic phase transitions in the thermal range of 330–440 °C.     

Toward optimization of a robust low-cost sulfonated-polyethersulfone containing layered double hydroxide for PEM fuel cells

Polyethersulphone (PES) is an aromatic thermoplastic, at low environmental impact, evaluated in this work as a promising candidate for new polymer electrolytes in the PEMFCs technology. A sulfonation procedure has been tuned in order to graft sulfonic acid groups on the polymer chains (sPES) and to make it hydrophilic. Homogeneous membranes with different polymer's sulfonation degrees (SD%) have demonstrated excellent mechanical properties and very low permeability toward methanol (important in the DMFCs), even if low proton conductivity. Nanocomposite sPES membranes were prepared by dispersion of highly hydrophilic lamellar particles such as layered double hydroxide (LDH) in the polymer. Deep investigations performed by a combination of PFG-NMR, EIS, XRD, DMA, and scanning electron microscopy have evidenced the exfoliation of the lamellae in polymer matrix. However, a certain anisotropy was evidenced both in the morphology and molecular diffusion, favored in the longitudinal direction (parallel to surface), while completely inhibited in the cross-section. This finding is most likely induced by the polymer structure, therefore particular attention must be paid to the choice of the filler and preparation of the composites. © 2019 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2019 , 136, 47884.     

Polyetherimide-LaNi5 composite films for hydrogen storage applications

This study investigates the preparation of polyetherimide (PEI) – LaNi₅ composites films for hydrogen storage. Prior to the polymer addition, LaNi₅ was ball-milled at different conditions (250, 350, and 450 RPM) and annealed at 500 °C for 1 h under vacuum. The composites were produced with BM-LaNi₅-350 (PEI/LaNi₅-350) and annealed BM-LaNi₅-350 (PEI/LaNi₅-350-TT). Membranes were successfully produced through solvent casting assisted by an ultrasonic bath. The particles dispersion and the film morphology did not change after hydrogenation cycles. In the H₂ sorption experiments at 43 °C and 20 bar, the films stored H₂ without incubation time; both samples reached a capacity of ~0.6 wt%. The H₂ sorption kinetics of PEI/LaNi₅-350 was comparable to that of BM-LaNi₅-350, whereas PEI/LaNi₅-350-TT presented significantly slower kinetics. LaNi₅ oxidation was hindered by PEI, showing that it can be explored to improve metal hydrides air resistance. The results demonstrated that PEI films filled with LaNi₅ are promising materials for hydrogen storage.     

Temperature/pH/magnetic triple‐sensitive nanogel–hydrogel nanocomposite for release of anticancer drug

Hydrogels, nanogels and nanocomposites show increasing potential for application in drug delivery systems due to their good chemical and physical properties. Therefore, we were encouraged to combine them to produce a new compound with unique properties for a long‐term drug release system. In this regard, the design and application of a nanocomposite hydrogel containing entrapped nanogel for drug delivery are demonstrated. To this aim, we first prepared an iron oxide nanocomposite nanogel based on poly(N‐isopropylacrylamide)‐co‐((2‐dimethylaminoethyl) methacrylate) (PNIPAM‐co‐PDMA) grafted onto sodium alginate (NaAlg) as a biocompatible polymer and iron oxide nanoparticles (ION) as nanometric base (PND/ION‐NG). This was then added into a solution of PDMA grafted onto NaAlg. Through dropwise addition of mixed aqueous solution of iron salts into the prepared polymeric solution, a novel hydrogel nanocomposite with excellent pH, thermal and magnetic responsivity was fabricated. The synthesized samples were fully characterized using Fourier transform infrared spectroscopy, thermogravimetric analysis, scanning electron microscopy with energy‐dispersive X‐ray analysis, vibrating sample magnetometry and atomic force microscopy. A mechanism for the formation of PNIPAM‐co‐PDMA/NaAlg‐ION nanogel–PDMA/NaAlg‐ION hydrogel and PND/ION nanogel is suggested. Swelling capacity was measured at various temperatures (25 to 45 °C), pH values (from 2 to 11) and magnetic field and under load (0.3 psi) and the dependence of swelling properties of the nanogel–hydrogel nanocomposite on these factors was well demonstrated. The release rate of doxorubicin hydrochloride (DOX) as an anticancer drug was studied at different pH values and temperatures in the presence and absence of a magnetic field. The results showed that these factors have a high impact on drug release from this nanocomposite. The result showed that DOX release could be sustained for up to 12.5 days from these nanocomposite hydrogels, significantly longer than that achievable using the constituent hydrogel or nanogel alone (<1 day). The results indicated that the nanogel–hydrogel nanocomposite can serve as a novel nanocarrier for anticancer drug delivery. © 2019 Society of Chemical Industry     

Studying the effect of organo-modified nanoclay loading on the thermal stability,flame retardant,anti-corrosive and mechanical properties of polyurethane nanocomposite for surface coating

Clay polyurethane nanocomposite (CPN) coating films were fabricated by uniformly dispersing nanoclay, organically modified with 25–30 wt.% octadecylamine in varying concentrations up to 5 wt.%, in a commercial two component, glossy, acrylic aliphatic polyurethane using ultrasonication. Organo-modified nanoclay was characterized by X-ray diffraction (XRD). The dispersion of the nanoclay into the matrix was investigated by scanning electron microscopy (SEM). CPN coating films were characterized by thermogravimetric analysis (TGA), and flame retardant, corrosion resistance and mechanical properties were also investigated. The XRD measurement indicated that, the organo-modified nanoclay particles were mainly constituted of montmorillonite with traces of quartz and calcite also found to be present. The SEM analysis showed that the nanoclay layers were dispersed and intercalated into the polyurethane coating. Thermogravimetric analysis showed that incorporating 5 wt.% organo-nanoclay into polyurethane considerably enhanced the thermal stability and increased the char residue to 14.11 wt.% relative to 4.58 for the sample without organo-nanoclay (blank polyurethane). The limiting oxygen index (LOI) test revealed that incorporation of organo-nanoclay led to a further increase in LOI values, which indicate an improvement in flame retardancy properties. The corrosion resistance also improved and this improvement increases with increase nanoclay wt.%. The mechanical resistance measurements demonstrated that the gloss of the CPN coating films slightly decreased, although hardness, adhesion and impact resistance of the CPN coating films improved with the incorporation of the organo-nanoclay.     

Impact of an Engineered Copper-Titanium Dioxide Nanocomposite and Parent Substrates on the Bacteria Viability,Antioxidant Enzymes and Fatty Acid Profiling

Due to the systematic increase in the production of nanomaterials (NMs) and their applications in many areas of life, issues associated with their toxicity are inevitable. In particular, the performance of heterogeneous NMs, such as nanocomposites (NCs), is unpredictable as they may inherit the properties of their individual components. Therefore, the purpose of this work was to assess the biological activity of newly synthesized Cu/TiO₂-NC and the parent nanoparticle substrates Cu-NPs and TiO₂-NPs on the bacterial viability, antioxidant potential and fatty acid composition of the reference Escherichia coli and Bacillus subtilis strains. Based on the toxicological parameters, it was found that B. subtilis was more sensitive to NMs than E. coli. Furthermore, Cu/TiO₂-NC and Cu-NPs had an opposite effect on both strains, while TiO₂-NPs had a comparable mode of action. Simultaneously, the tested strains exhibited varied responses of the antioxidant enzymes after exposure to the NMs, with Cu-NPs having the strongest impact on their activity. The most considerable alternations in the fatty acid profiles were found after the bacteria were exposed to Cu/TiO₂-NC and Cu-NPs. Microscopic images indicated distinct interactions of the NMs with the bacterial outer layers, especially in regard to B. subtilis. Cu/TiO₂-NC generally proved to have less distinctive antimicrobial properties on B. subtilis than E. coli compared to its parent components. Presumably, the biocidal effects of the tested NMs can be attributed to the induction of oxidative stress, the release of metal ions and specific electrochemical interactions with the bacterial cells.     

Wear and Creep Characteristics of a Carbon‐Derived Si3N4/SiC Micro/Nanocomposite

In the presented work some properties of a recently developed Si₃N₄/SiC micro/nanocomposite have been investigated. The material was tested using a pin on disc configuration. Under unlubricated sliding conditions using Si₃N₄ pin at 50 % humidity, the friction coefficient was in the range of 0,6 ‐ 0,7. The reduction of humidity resulted in a lower coefficient of friction, in vacuum the coefficient of friction had a value of about 0,6. The wear resistance in vacuum was significantly lower then that in air. The wear patterns on the Si₃N₄+SiC disc revealed that mechanical fracture was the wear controlling mechanism. Creep tests were realized in four point bending configuration in the temperature interval 1200‐1400 °C at stresses 50,100 and 150 MPa and the minimal creep deformation rate was established for each stress level. The activation energy, established from the minimal creep deformation had a value of about 360 kJ/mol and the stress exponent values were in the range of 0.8‐1.28. From the achieved stress exponents it can be assumed that under the studied load/temperature conditions the diffusion creep was the most probable creep controlling mechanism.     

原位插层聚合制备PVC/蒙脱土纳米复合材料

采用氯乙烯单体直接插层到蒙脱土中进行原位插层聚合，制备纳米复合材料，并用小角X射线衍射（XRD）、扫描电子显微镜（SEM）和电子探针技术对复合材料进行了结构表征。实验结果表明：采用原位插层聚合法制得的PVC／蒙脱土（MMT）复合材料为剥离型纳米复合材料。     

Poly(butylene terephthalate)–clay nanocomposites prepared by melt intercalation: morphology and thermomechanical properties

Nanocomposites based on poly(butylene terephthalate) (PBT) and an organoclay (Cloisite 30B) were prepared by melt blending using a twin‐screw extruder. Two kinds of PBTs, ie PBT‐A and PBT‐B, with different inherent viscosities (η_inh), were used for this study (η_inh of PBT‐A and PBT‐B were 0.74 and 1.48, respectively). Dispersion of the clay layers in the PBT nanocomposites was characterized by using X‐ray diffraction (XRD) and transmission electron microscopy (TEM). Tensile and dynamic mechanical properties and non‐isothermal crystallization temperatures of the nanocomposites were also examined. Nanocomposites based on the higher‐viscosity PBT (PBT‐B) showed a higher degree of exfoliation of the clay and a higher reinforcing effect when compared to the composites based on the lower‐viscosity PBT (PBT‐A). The clay nanolayers dispersed in PBT matrices lead to increases in the non‐isothermal crystallization temperatures of the PBTs, with such increases being more significant for the PBT‐B nanocomposites than for the PBT‐A nanoocomposites. Copyright © 2004 Society of Chemical Industry     

Complex formation of montmorillonite clay with polymers. Part 2: The use of montmorillonite clay–vinyl monomer complex as a comonomer in the copolymerization reaction of styrene–acrylonitrile monomers

The bulk copolymerization of styrene–acrylonitrile monomers using styrene‐N⁺–montmorillonite complex as a comonomer in the polymerization was studied. The X‐ray diffraction (XRD) analysis showed that part of the styrene‐N⁺–montmorillonite complex remained non‐dispersed (immiscible) and the copolymer was excluded from the interlayer of the immiscible part of the clay. The successive chemical extraction process revealed that a reasonable amount of the styrene–acrylonitrile copolymer was directly attached to the styrene‐N⁺–montmorillonite complex and enveloped the clay. Highly exfoliated clay lamella and nanospheres (3–5 nm) were observed by transmission electron microscopy (TEM). The montmorillonite clay assume two different morphologies, immiscible and exfoliated, on the basis of the XRD and TEM data. A simple method of calculation of the ratio of the exfoliated/immiscible amounts of the clay indicated that the amount of the styrene‐N⁺–montmorillonite complex exfoliated into separate lamella was 40 % (w/w) of the amount of the clay samples containing 2 % of the (styrene‐N⁺–montmorillonite complex) clay. This amount of exfoliated clay decreases with the increase of the concentration of the clay. The presence of the styrene‐N⁺–montmorillonite clay in the copolymerization reaction had a minor effect on both the copolymer composition and the molecular weight. Modification of the clay with the derivatized styrene monomer can achieve a nanocomposite using a percentage no more than 4 % (w/w) of complex in the copolymer. Copyright © 2004 Society of Chemical Industry