Preparation and electrochemical characterization of Ti-based amorphous metallic glass with high strength

Ti-based amorphous metallic glasses have excellent mechanical, physical, and chemical properties, which is an important development direction and research hotspot of metal composite reinforcement. As a stable, simple, efficient, and large-scale preparation technology of metallic powders, the gas atomization process provides an effective way of preparing amorphous metallic glasses. In this study, the controllable fabrication of a Ti-based amorphous powder, with high efficiency, has been realized by using gas atomization. The scanning electron microscope, energy-dispersive spectrometer, and X-ray diffraction are used to analyze surface morphology, element distribution, and phase structure, respectively. A microhardness tester is used to measure the mechanical property. An electrochemical workstation is used to characterize corrosion behavior. The results show that as-prepared microparticles are more uniform and exhibit good amorphous characteristics. The mechanical test shows that the hardness of amorphous powder is significantly increased as compared with that before preparation, which has the prospect of being an important part of engineering reinforced materials. Further electrochemical measurement shows that the corrosion resistance of the as-prepared sample is also significantly improved. This study has laid a solid foundation for expanding applications of Ti-based metallic glasses, especially in heavy-duty and corrosive domains.     

Electrochemical Quantification of Neurotransmitters in Single Live Cell Vesicles Shows Exocytosis is Predominantly Partial

Exocytosis plays an essential role in the communication between cells in the nervous system. Understanding the regulation of neurotransmitter release during exocytosis and the amount of neurotransmitter content that is stored in vesicles is of importance, as it provides fundamental insights to understand how the brain works and how neurons elicit a certain behavior. In this minireview, we summarize recent progress in amperometric measurements for monitoring exocytosis in single cells and electrochemical cytometry measurements of vesicular neurotransmitter content in individual vesicles. Important steps have increased our understanding of the different mechanisms of exocytosis. Increasing evidence is firmly establishing that partial release is the primary mechanism of release in multiple cell types.     

Effect of spheroidized microstructure on the impact toughness and electrochemical performance of a high-carbon steel

The influence of cementite spheroidization on the impact toughness and electrochemical properties of a high-carbon steel has been thoroughly investigated in this study. Heavy warm rolling, followed by 2 h of annealing, has resulted in near-complete spheroidization, leading to a microstructure consisting of nano-cementite globules dispersed in the ultrafine-grained ferritic matrix. The Charpy impact test exhibited superior impact toughness with increased spheroidization. It is validated by the presence of abundant dimples in the fractographs of spheroidized specimens, in contrast to the as-received one that experienced a brittle failure due to its lamellar pearlitic structure. Potentiodynamic polarization and electrochemical impedance spectroscopy (EIS) carried out in a 3.5% NaCl solution revealed that the corrosion resistance of the alloy gets improved with the increase in the degree of spheroidization. This is attributed to the lower susceptibility of the spheroidized specimen to microgalvanic corrosion owing to the minimum area of contact between nano-spheroidized cementite and ferrite, as elucidated with the help of EIS results aided by equivalent electrical circuit model.     

Manufacturing catalyst-coated membranes by ultrasonic spray deposition for PEMFC: Identification of key parameters and their impact on PEMFC performance

This study deals with the manufacturing of catalyst-coated membranes (CCMs) for newcomers in the field of coating. Although there are many studies on electrode ink composition for improving the performance of proton-exchange membrane fuel cells (PEMFCs), there are few papers dealing with electrode coating itself. Usually, it is a know-how that often remains secret and constitutes the added value of scientific teams or the business of industrialists. In this paper, we identify and clarify the role of key parameters to improve coating quality and also to correlate coating quality with fuel cell performance via polarization curves and electrochemical active surface area measurements. We found that the coating configurations can affect the performance of lab-made CCMs in PEMFCs. After the repeatability of the performance obtained by our coating method has been proved, we show that: (i) edge effects, due to mask shadowing - cannot be neglected when the active surface area is low, (ii) a heterogeneous thickness electrode produces performance lower than a homogeneous thickness electrode, and (iii) the origin and storage of platinum on carbon powders are a very important source of variability in the obtained results.     

300M超高强钢在中性盐雾环境中的腐蚀行为及机制

摘要：为了研究300M超高强钢在中性盐雾环境中的腐蚀行为及腐蚀机制，采用失重法，宏观、微观腐蚀形貌分析，三维表面轮廓分析及电化学分析的研究方法，来表征腐蚀实验现象并进行分析。结果表明：300M超高强钢在中性盐雾环境中的腐蚀产物为FeOOH、Fe2O3、Fe(OH)3和Fe3O4；腐蚀速率随着腐蚀时间逐渐降低，腐蚀后期（72h）腐蚀速率降低50%；腐蚀初期以点蚀为主，点蚀坑通过横向扩展，逐渐发展为后期的均匀腐蚀，腐蚀表面形貌呈沟壑状；外腐蚀层对基体的保护能力很弱，Cr元素在锈层靠近基体的一侧偏聚使内腐蚀层具有一定的抗腐蚀性。     

航空发动机复杂扭曲叶片分步电解加工研究

为实现复杂扭曲叶片在较小间隙下的稳定加工,提出了一种分步式电解加工的工艺方法,建立了复杂扭曲叶片小间隙(0.2 mm)和大间隙下(0.5 mm)扭曲流道的流道模型,采用有限元法进行了流场仿真研究,结果表明增加流道间隙可以解决流道中涡流和流场紊乱的问题。开展了复杂扭曲叶片小间隙连续式加工和分步式加工的试验研究。结果表明,采用小间隙连续式加工,当阴极进给至3.8 mm位置时,在叶片排气边靠近叶根流道扭曲处出现短路打火情况;而采用分步式加工方式能够实现加工的顺利进行。     

钛基Ce掺杂SnO_2-RuO_2电极的制备及其对焦化废水的电解处理

采用溶胶-凝胶法制备了经稀土元素Ce掺杂改性的Ti/RuO_2-SnO_2-Ce电极,利用SEM、XRD、EDS等分析方法对电极表面的形貌、物相和涂层成分进行了表征,利用CV曲线、LSV曲线等检测手段对电极的电化学性能进行了测试。以Ti/RuO_2-SnO_2-Ce电极为阳极,钛板为阴极,构建电化学氧化反应装置,并采用其对焦化废水进行电解处理。结果表明,Ti/RuO_2-SnO_2电极经稀土Ce改性后极板表面活性位点数量明显增大,金属涂层的结晶化程度明显增强,电极的催化氧化活性显著提高。室温条件下,保持pH值为7.83,在电流密度为30mA/cm~2,电解时间为30min时,焦化废水经电解处理后COD去除率可达91.63%,TOC去除率可达66.22%,UV254值下降到0.921。