Multi-criteria analysis for screening of reversible metal hydrides in hydrogen gas storage and high pressure delivery applications

Metals and alloys forming reversible hydrides with hydrogen gas are potential building blocks for compact, solid state hydrogen storage systems. Based on the materials’ thermodynamic characteristics, their use as temperature-swing gas compression and delivery systems in the hydrogen economy is also possible. Given the wide variety of materials developed and tested at laboratory and pilot scales, a harmonized method of selecting the feasible material(s) for a particular real-life application is required. This study proposes a system selection framework based on a normalized, multi-criteria metric. Using calculated values of multi-criteria metric, multi-criteria screening and ranking of potential materials has been demonstrated for a particular use case. It is found that the alloy TiMn_1.52 having value of additive metric between 0.25 and 0.35 represents the best material for a single stage system. The alloy pair CaNi₅–Ti_1.5CrMn represents the best alternative for a two-stage system with additive metric values between 0.63 and 0.82. Energy and economic characteristics of the metal hydride gas compression and delivery systems are evaluated and compared with an equivalent mechanical compression system producing the same final effect (i.e., delivery of a given quantity of gas at a defined pressure).     

Theoretical prediction of structure,electronic and optical properties of VH2 hydrogen storage material

The vanadium hydrides have better hydrogen storage capacity in comparison to the other metal hydrides. Although the structure of VH₂ hydride has been reported, the structural stability, electronic and optical properties of VH₂ hydride are unclear. To solve these problems, we apply the first-principles method to study the structural stability, electronic and optical properties of VH₂ hydrides. Similar to the metal dihydrides, four possible VH₂ hydrides such as the cubic (Fm-3m), tetragonal (I4/mmm), tetragonal (P4₂/mnm) and orthorhombic (Pnma) are designed. The result shows that the cubic VH₂ hydride is a thermodynamic and dynamical stability. In particular, the tetragonal (I4/mmm) and the orthorhombic (Pnma) VH₂ hydrides are firstly predicted. It is found that these VH₂ hydrides show metallic behavior. The electronic interaction of V (d-state)-H (s-state) is beneficial to improve the hydrogen storage in VH₂ hydride. In addition, the formation of V–H bond can improve the structural stability of VH₂ hydride. Based on the analysis of optical properties, it is found that all VH₂ hydrides show the ultraviolet response. Compared to the tetragonal and orthorhombic VH₂ hydrides, the cubic VH₂ hydride has better storage optical properties. Therefore, we believe that the VH₂ hydride is a promising hydrogen storage material.     

Porous CoNiOOH nanosheets derived from the well-mixed MOFs as stable and highly efficient electrocatalysts for water oxidation

The development of efficient and stable electrocatalysts is of great significance for improving water splitting. Among them, transition metal oxyhydroxides show excellent performance in oxygen evolution reactions (OER), but there are certain difficulties in direct preparation. Recently, Metal–organic frameworks (MOFs) as precatalysts or precursors have shown promising catalytic performance in OER and can be decomposed under alkaline conditions. Therefore, using a mild and controllable way to convert MOFs into oxyhydroxides and retaining the original structural advantages is crucial for improving the catalytic activity. Herein, a rapid electrochemical strategy is used to activate well-mixed MOFs to prepare Co/Ni oxyhydroxide nanosheets for efficient OER catalysts, and the structural transformation in this process was investigated in detail by using scanning electron microscope, X-ray diffraction, Raman, X-ray photoelectron spectroscopy and electrochemical methods. It is discovered that electrochemical activation can promote ligand substitution of well-mixed MOFs to form porous oxyhydroxide nanosheets and tune the electronic structure of the metal (Co and Ni), which can lead to more active site exposure and accelerate charge transfer. In addition, the change of structure also improves hydrophilicity, as well as benefiting from the strong synergistic effect between multiple species, the optimal a-MCoNi–MOF/NF has excellent OER performance and long-term stability. More obviously, the porous CoNiOOH nanosheets are formed in situ during electrochemical activation process through structural transformation and acts as the active centers. This work provides new insights for mild synthesis of MOFs derivatives and also provides ideas for the preparation of highly efficient catalysts.     

Nonlinearity in regulating the metal to insulator transition of ReNiO3 towards low temperature range

Among the existing material family of the correlated oxides, the rare earth nickelates (ReNiO₃) exhibit broadly adjustable metal to insulator transition (MIT) properties that enables correlated electronic applications, such as thermistors, thermochromics, and logical devices. Nevertheless, how to accurately control the critical temperature (T_MIT) of ReNiO₃ via the co-occupation of the rare-earth elements is yet worthy to be further explored. Herein, we demonstrate the non-linearity in adjusting the T_MIT of ReNiO₃ towards lower temperatures via introducing Pr co-occupation within ReNiO₃ (e.g., Pr_xNd_1-xNiO₃ and Pr_xSm_1-xNiO₃) as synthesized by KCl molten-salt assisted high oxygen pressure reaction approach. Although the T_MIT is effectively reduced via Pr substitution, it does not strictly follow a linear relationship, in particular, when there is large difference in the ionic radius of the co-occupation rare-earth elements. Furthermore, the most significant deviation in T_MIT from the expected linear relationship appears at an equal co-occupation ratio of the two different rare-earth elements, while the abruption in the variation of resistivity across T_MIT is also reduced. The present work highlights the importance to use adjacent rare-earth elements with co-occupation ratio away from 1:1 for achieving more linear adjustment in designing the metal to insulator transition properties for ReNiO₃.     

Study on single and binary catalytic systems of pyridine-imine catalysts based on nickel and iron in synthesis of reactor blends and low-density polyethylene nanocomposites

In the presence of modified methylaluminoxane as cocatalyst, the behavior of a binary catalytic system based on pyridine-imine nickel ( N ) and iron ( F ) catalysts was evaluated in order to reach a proper mixture of polyethylene (PE). A computational study along with kinetic profile suggested that the catalyst F with higher electron affinity (A) and electrophilicity (ω) in the methyl cationic active center and stronger interaction with the monomer led to high integrated monomer consumption and higher activity. In addition, the samples produced by the mixture of catalysts showed a higher value of [19.4 × 10⁴ g (PE) mol (Fe+Ni)⁻¹ h⁻¹)], melting point (127.8 °C), and crystallinity extent (41.29%) than the samples produced by the single catalysts. The addition of multiwalled carbon nanotubes (MWCNT) into the polymerization media reduced the activity of catalysts [from 7.50 × 10⁴ to 0.66 × 10⁴ g (PE) mol (Fe+Ni)⁻¹ h⁻¹] and the thermal properties of the low-density polyethylene nanocomposite samples. However, the sample containing 2.33% MWCNT_20-30 improved the total thermal stability of the neat polyethylene blend up to 400 °C. Scanning electron microscope images of the samples demonstrated irregular to virtually uniform morphologies were obtained through the in situ and solution-mixing techniques. © 2019 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2019 , 136, 47376.     

Microstructure,wear and corrosion characteristics of multiple-reinforced (SiC–B4C–Al2O3) Al matrix composites produced by liquid metal infiltration

In this study, AA7075 aluminum matrix composites reinforced with the combination of SiC, Al₂O₃, and B₄C particles were fabricated by the liquid metal infiltration method. The effects of the relative ratio of B₄C and Al₂O₃ particles on the microstructural, wear, and corrosion features of the composite samples were analyzed using XRD, light metal microscopy, SEM, EDS, Brinell hardness, ball-on-disc type tribometer, and potentiodynamic polarization devices. It was determined that infiltration occurred more successfully, and homogenously distributed particles with reduced porosity were obtained as the amount of Al₂O₃ increased. Worn surface studies revealed that the specimens were predominantly worn by abrasion and adhesion. The increase in B₄C/Al₂O₃ ratio caused a decrease in the hardness and wear strength, whereas it increased the corrosion resistance.     

Ablation behavior of thin-blade co-deposited C/Cx-SiCy composites under the influence of the complex fluid conditions of the oxyacetylene torch

This paper offers a new way of testing the ablation property of material under an oxyacetylene torch using a thin-blade specimen, which costs much less time to reach the maximum temperature and provides a harsh turbulence fluid field that's closer to reality. The thin-blade specimen experiences a higher turbulent intensity than the traditional disk-like specimen, leading to more efficient heat exchange. The fluid field simulation agrees with the testing results. In addition, we manage to synthesize the C/Cx-SiCy composites with the co-deposition chemical vapor infiltration (CVI) method. The C/Cx-SiCy composites exhibit a similar anti-ablation property as C/C composites and consist of enough SiC phase simultaneously, combining the advantages of both C/C composites and C/SiC composites. The thin-blade C/Cx-SiCy composites show a lower linear ablation rate (1.6 μm/s) than C/C composites (4.1 μm/s) and C/SiC composites (19.6 μm/s) during the oxyacetylene test. The glass layer formed on the surface of C/Cx-SiCy could cling to the bulk material instead of peeling off due to the high PyC content in the matrix could protect the SiO₂ from blowing away.     

Environmental effects on the strength and impact damage resistance of alumina based oxide/oxide ceramic matrix composites

In this study the effects of high temperature and moisture on the impact damage resistance and mechanical strength of Nextel 610/alumina silicate ceramic matrix composites were experimentally evaluated. Composite laminates were exposed to either a 1050°C isothermal furnace-based environment for 30 consecutive days at 6 h a day, or 95% relative humidity environment for 13 consecutive days at 67°C. Low velocity impact, tensile and short beam strength tests were performed on both ambient and environmentally conditioned laminates and damage was characterized using a combination of non-destructive and destructive techniques. High temperature and humidity environmental exposure adversely affected the impact resistance of the composite laminates. For all the environments, planar internal damage area was greater than the back side dent area, which in turn was greater than the impactor side dent area. Evidence of environmental embrittlement through a stiffer tensile response was noted for the high temperature exposed laminates while the short beam strength tests showed greater propensity for interlaminar shear failure in the moisture exposed laminates. Destructive evaluations exposed larger, more pronounced delaminations in the environmentally conditioned laminates in comparison to the ambient ones. External damage metrics of the impactor side dent depth and area directly influenced the post-impact tensile strength of the laminates while no such trend between internal damage area and residual strength could be ascertained.     

A microfluidic approach for development of hybrid collagen-chitosan extracellular matrix-like membranes for on-chip cell cultures

To advance organ-on-a-chip development and other areas befitting from physiologically-relevant biomembranes,a microfluidic platform is presented for synthesis of biomembranes during gelation and investigation into their role as extracellular matrix supports.In this work,high-throughput studies of collagen,chitosan,and collagen-chitosan hybrid biomembranes were carried out to characterize and compare key properties as a function of the applied hydrodynamic conditions during gelation.Specifically,depending on the biopolymer material used,varying flow conditions during biomembrane gelation caused width,uniformity,and swelling ratio to be differently affected and controllable.Finally,cell viability studies of seeded fibroblasts were conducted,thus showing the potential for biological applications.     

Topology optimization of flexure hinges with a prescribed compliance matrix based on the adaptive spring model and stress constraint

This paper focuses on the configuration design of flexure hinges with a prescribed compliance matrix and preset rotational center position. A new method for the topology optimization of flexure hinges is proposed based on the adaptive spring model and stress constraint. The hinge optimization model is formulated by maximizing the bending displacement with a spring while optimizing the compliance matrix to a prescribed value. To avoid numerical instability, an artificial spring is used as an auxiliary calculation, and a new strategy is developed for adaptively adjusting the spring stiffness according to the prescribed compliance matrix. The maximum stress of flexure hinge is limited by using a normalized P-norm of the effective von Mises stress, and a position constraint of rotational center is proposed to predetermine the position of the rotational center. In addition, to reduce the error of the stress measurement, a simple but effective filtering method is presented to obtain a complete black-and-white design. Numerical examples are used to verify the proposed method. Topology results show that the obtained flexure hinges have the prescribed compliance matrix and preset rotational center position while also meeting the stress requirements.