Selective Oxidation of Isobutene over CsFeCoBiMnMoOx Mixed Oxide Catalyst

Mixed oxide catalyst Cs0.1Fe2Co6BiMnMo12Ox was prepared by the coprecipitation method.Selective oxidation of isobutene was carried out in a fixed-bed reactor over Cs0.1Fe2Co6BiMnMo12Ox.The results showed that the catalyst had high catalytic activity. Under the optimum reaction conditions(n(i-C4):n(O2)=1:2-1:4, space velocity=180 h^-1, T=360℃), the yields of methacrolein and methacrylic acid can reach 80% and 8%, respectively. The total yield of liquid products (methacrolein, methacrylic acid and acetic acid) can reach about 90%.     

MOLECULAR ENGINEERING STUDIES ON NONTHROMBOGENIC BIOMATERIALS——A NOVEL CLASS OF NONTHROMBOGENIC BIOMATERIALS WITH ZWITTERIONIC STRUCTURE OF CARBOXYBETAINES

N,N-dimethyl-N-methacryloyloxyethyl-N-carboxyethyl ammonium (DMMCA) was graft-copolymerized onto the surface of segmented poly(ether urethane) (SPEU) and PE film. The carboxybetaine structure on SPEU and PE film surfaces was confirmed by ATR-FTIR, XPS and water contact angle measurements. Through the experiments with platelet adhesion and protein adhesion assay in vitro, the two materials studied, including poly-DMMCA gel, all show excellent nonthrombogenicity. This confirms once again that the zwitterionic molecular structure on the surfaces of materials is essential for improving their nonthrombogenicity and biocompatibility.     

Cs-Fe-Co-Bi-Mn-Mo复合氧化物选择性催化氧化异丁烯

Mixed oxide catalyst Cs0.1 Fe2Co6BiMnMo12 Ox was prepared by the interprecipitation method, then the catalyst was calcined at different temperature. Selective oxidation of isobutene was carried out in a fixed-bed reactor. The results showed that the catalyst has high catalytic activity. Under the optimum reaction conditions ( n(-C4^= ) : n(O2) = 1:2-1:4, space velocity = 180h^-1, T = 360℃ ), the yield of methacmlein and methacrylic reached 80%, 8 %,respectively. The total yields of liquid products( methacrolein, methacrylic acid and acetic acid) reached about 90%.     

Cu/MoO3-TiO2/SiO2上光催化CO2和C3H8合成异丁烯醛的研究

采用表面改性法和等体积浸渍法制备了金属修饰的负载型复合半导体材料Cu/MoO3-TiO2/SiO2, 用X射线衍射、 比表面积测定、 红外光谱、 拉曼光谱和紫外-可见漫反射等技术对固体材料的结构、 吸光性能和化学吸附性能进行了表征, 研究了该材料对CO2和丙烷合成异丁烯醛的光促表面催化规律. 结果表明, 半导体活性组分MoO3和TiO2在所制备的催化剂Cu/MoO3-TiO2/SiO2表面形成化学键, 并存在多种活性吸附位; 金属Cu的修饰拓展了固体材料对光源的响应范围, 提高了反应体系的吸光能力; 固体材料对CO2和丙烷的有效吸附使其在较低温度下就能促进异丁烯醛的紫外光化学合成, 反应选择性达到85％左右. 根据实验结果对光促CO2和丙烷表面催化合成异丁烯醛的机理进行了讨论.     

CO2氧化异丁烷制异丁烯用Pd/V2O5-SiO2催化剂

 利用表面化学反应改性法制备了不同V2O5负载量的V2O5-SiO2表面复合物载体,进而采用等体积浸渍法制备了负载型Pd催化剂. 用N2吸附、 X射线衍射、透射电镜、 X射线光电子能谱、程序升温脱附、化学吸附-红外光谱和微反技术对系列Pd/V2O5-SiO2催化剂的比表面积、晶相结构、价态、异丁烷的化学吸附性能和CO2部分氧化异丁烷制异丁烯的催化性能进行了研究. 结果表明, Pd/V2O5-SiO2催化剂中的钒以V5+形式存在, V5+在催化剂表面形成活性位V=O, 其中 V=O 晶格氧与 i-C4H10分子的-CH3 和-CH 中的H产生化学吸附作用; 催化剂中金属Pd与V4+协同作用使CO2在催化剂上产生了卧式吸附态; 晶格氧参加了催化氧化反应,催化剂中 V5+←→V4+ 的变化构成了催化反应的氧化还原过程. 在525 ℃, CO2/i-C4H10体积比为1和空速为 1200 h-1的条件下,以Pd/25%V2O5-SiO2为催化剂时异丁烷转化率为22.8%, 异丁烯选择性为89.1%.     

Controlled/“Living “Radical Polymerization of(-)-Menthyl Methacrylate

The atom transfer radical polymerization(ARP)of (-)-menthyl methacrylatc((-)-MnMA) mediated by CuCl/bipyridine and ethy1 2-bromopropionate or 1-phenylethyl bromide in THF system has been studied.The dependence of the specific rotation on molecular weight and the CD of Poly((-)-MnMA) thus obatined was investigated.     

铑配合物催化丁烯氢甲酰化性能的研究

制备了一系列铑配合物,并对其催化丁烯氢甲酰化的催化性能进行了研究.在1-丁烯的反应中,RhCl(PPh3)3和trans-RhCl(CO)(PPh3)2的反应速度很慢,而RhH(CO)(PPh3)3、Rh(CO)2(acac)和 Rh(CO)(acac)(PPh3)三者反应速度都很快.而不同丁烯原料氢甲酰化的反应速度也各不相同,反应速度依次为1-丁烯》2-丁烯》异丁烯.     

H_2O/TiCl_4/ED体系引发异丁烯控制正离子聚合中的影响因素研究

在亲核试剂(ED)如吡啶(Py)、N,N-二甲基乙酰胺(DMA)或三乙胺(TEA)存在下,由引发剂H2O和共引发剂TiCl4组成引发体系,在二氯甲烷/正己烷混合溶剂中进行异丁烯(IB)正离子聚合,考察了溶剂极性、聚合温度及异丁烯浓度对聚合反应转化率、产物分子量和分子量分布的影响.试验结果表明,随聚合体系溶剂极性增大,聚合速率加快,相近转化率时聚合产物的分子量分布变窄.随着聚合温度降低,聚合速率明显提高,聚合物的分子量增加,活化能为负值,活性链端发生链转移或链终止等副反应的几率减小,当聚合温度为-60℃时,可以抑制活性链端的β-H脱除反应和链转移副反应,并得到大分子链末端全部为叔氯基团的聚异丁烯(PIB).当[IB]0≤2.5mol/L时,随[IB]0增加,聚合转化率有所增加,聚合产物的GPC谱图均为单峰分布,分子量增大,而分子量分布基本保持不变,对于加入Py的聚合体系,分子量分布指数在1.33~1.45范围内,对于加入TEA的聚合体系,分子量分布指数在1.47~1.60范围内,并求出在加入Py和TEA的聚合体系中活性链向单体的链转移常数CM分别为5.5×10-4和6.6×10-4.     

无粘结剂ZSM-11催化剂上异丁烯直接胺化生成叔丁胺

叔丁胺是一种重要的化工原料和中间体,广泛应用于制备橡胶促进剂、医药、农药和着色剂等下游产品.异丁烯在分子筛催化剂上直接胺化生产叔丁胺是一个经济环保过程,其中ZSM-5和BEA分子筛的催化性能优于其它系列分子筛.ZSM-11与ZSM-5分子筛具有相似的孔道结构,我们以前的实验结果表明,与ZSM-5相比,ZSM-11表现出更优越的芳构化反应性能,在干气中乙烯低温芳构化方面也有明显优势.在此基础上,我们进行无粘结剂ZSM-11分子筛催化剂合成,并应用于异丁烯直接胺化生产叔丁胺反应.传统水热技术合成的分子筛通常为粉末,机械强度不能达到实际应用的要求,在工业化过程中分子筛粉末一般需要加入粘结剂成型使其具备一定的机械强度和形状,但是粘结剂会降低分子筛催化剂的活性和选择性,有可能会引发一些副反应,因此无粘结剂分子筛催化剂引起人们广泛关注.无粘结剂分子筛是指分子筛颗粒中不含惰性粘结剂或只含有少量粘结剂,主要依靠分子筛晶粒间的相互作用支撑存在,具有一定形状、尺寸和机械强度的催化材料.无粘结剂分子筛催化剂中分子筛含量较高,可利用的有效表面积较大,在离子交换及工业催化等方面具有明显优势.本文采用水热合成的ZSM-11分子筛原粉与二氧化硅机械混合(ZSM-11/SiO2=70/30)挤条后,通过气固相合成法制备了无粘结剂ZSM-11分子筛催化剂(Cat-C).作为对比,还分别制备了ZSM-11和SiO2机械混合(ZSM-11/SiO2=70/30)样品HZSM-11+SiO2及ZSM-11和氧化铝机械混合(ZSM-11/Al2O3=70/30)样品HZSM-11+Al2O3.利用X射线衍射、透射电镜、NH3程序升温脱附和吸附吡啶红外光谱等对分子筛催化剂的物理化学性能进行了表征.同时,以这些分子筛样品为催化剂,在固定床反应装置上进行了异丁烯胺化反应评价,反应条件为270℃,5.0 MPa,氨烯比为4和异丁烯空速0.5 h?1.结果表明,与HZSM-11+SiO2和HZSM-11+Al2O3相比,Cat-C上叔丁胺生成速率最高.关联催化剂物化性能和反应性能发现,催化剂孔道结构与叔丁胺生成并不存在明显的关联性,而较多的Br?nsted酸和较少的Lewis酸才是Cat-C具有良好反应性能的主要原因.具有一定机械强度的无粘结剂ZSM-11分子筛催化剂制备简单,在异丁烯直接胺化过程中叔丁胺生成速率高,具有很好的工业化应用前景.     

异丁烷直接脱氢制异丁烯催化剂研究进展

从热力学和反应机理角度概述了异丁烷直接脱氢和氧化脱氢的差异;从活性中心性质、失活与再生、助催化剂以及载体方面,综述了目前广泛研究的异丁烷直接脱氢制异丁烯催化剂,包括PtSn-、CrOx-、GaOx基和金属硫化物催化剂,并分析了各类催化剂的优缺点及目前的研究方向;简述了其他类型的脱氢催化剂,包括Mo/MgAl2O4、碳基材料、Co-、Ni2P-、VOx基催化剂等;分析了目前脱氢技术面临的问题以及未来的研究方向。