涂料用纯丙乳液的性能研究

以甲基丙烯酸甲酯(MMA)、丙烯酸丁酯(BA)和甲基丙烯酸(MA)为主要原料,利用半连续乳液聚合工艺,制备了一种涂料用纯丙乳液基料;考察了乳化剂、引发剂用量及pH值对产物性能的影响。结果表明,当w(乳化剂)=3%,w(引发剂)=0.35%,pH在8~9左右时,涂膜的吸水率达到7.9%,残余单体量<0.5%,水稀释稳定性,钙离子稳定性,冻融稳定性均通过测试,纯丙乳液具有较好的综合性能。     

丙烯酸/α-甲基丙烯酸/丙烯酰胺共聚物智能水凝胶的合成及评价

由丙烯酸（AA）、α-甲基丙烯酸（MAA）和丙烯酰胺（AM）合成了具有很好DH敏感性和一定温度敏感性的智能水凝胶，考察了合成温度、丙烯酰胺、交联剂和引发剂用量对制备的水凝胶溶胀性能的影响。结果表明，在60℃下，单体从和MAA用量分别为100mmol和75mmol时，单体AM、交联剂和引发剂用量分别为反应物总质量的32．8％、0．2％和0．4％时，制备的水凝胶溶胀性能最好。考察了介质的离子浓度、pH值和温度对水凝胶溶胀比的影响，结果表明，离子浓度越大，水凝胶的溶胀比越小；水凝胶具有一定的DH可逆性。     

马来酸酐-丙烯酸含膦共聚物的合成及阻垢性能

以水为溶剂，马来酸酐（MA）、丙烯酸（AA）为单体，过硫酸盐-次磷酸盐氧化还原体系为引发剂，合成马来酸酐-丙烯酸含膦共聚物阻垢剂。研究了聚合条件对共聚物阻垢性能的影响，确定最佳聚合条件为：马来酸酐与丙烯酸摩尔比1：3，次磷酸盐用量为单体总质量的20％，引发剂用量为单体总质量的10％，反应温度90℃，反应时间4h。在此反应条件下合成的聚合物对CaCO3和CaSO4有较好的阻垢性能。     

Inhibition of radical polymerization in solvent‐based systems (security of solvent‐based radical polymerization of PSA‐acrylic in a plant reactor)

This article shows the influence of some chain‐transfer agents as inhibitors for acrylic solvent‐based polymerization. These chain‐transfer agents can offer significant advantages, as outlined below. The following chain‐transfer agents were studied to stop or slow down the polymerization process in the case of a runaway: n‐dodecyl mercaptan, trimethylolpropane‐trimercaptoacetate, phenothiazine, diphenylphenylen diamine, cuprum oxide, isopropanol, toluene, and carbon tetrachloride. Synthesized pressure‐sensitive adhesive based on acrylic polymers and containing 2‐ethylhexyl acrylate, methyl acrylate, and acrylic acid were used for the production of self‐adhesives with high cohesion. The polymerization was accomplished in ethyl acetate. © 2002 Wiley Periodicals, Inc. J Appl Polym Sci 87: 1354–1357, 2003     

乙烯基硅氧烷改性苯丙乳液的研究

在苯乙烯 -丙烯酸酯乳液共聚反应后期 ,加入少量乙烯基硅氧烷 ,制得改性苯丙乳液 ,通过红外光谱初步确定了聚合物结构。研究了反应温度、反应时间、有机硅加入方式、乳化剂用量等因素对反应进程、乳液稳定性及涂膜性能的影响。     

水溶性丙烯酸涂料的环氧树脂改性

本实验论述了水溶性丙烯酸钢铁底漆涂料制备、性能以及用环氧树脂对其进行改性。原水溶性丙烯酸钢铁底漆涂料在进行耐盐雾测定试验时仅为 72h ,未通过国家规定标准。本实验的目的在于 ,以丙烯酸树脂为主要成膜物质 ,加入其他的辅助成膜物质 ,如环氧树脂来改善其抗盐雾、抗腐蚀、耐候等性能。结果表明 ,一定温度下在水溶性丙烯酸钢铁底漆涂料中加入 1/ 7的环氧树脂后 ,经测定其耐盐雾性可达 10 6h ,达到了国家的规定标准     

Structural acrylic adhesives for the sheet steel fabrication industries

Recent developments in rubber-toughened structural acrylic adhesives now offer sheet steel fabricators the opportunity to replace conventional metal fastening techniques such as spot welding with lower cost, durable, more versatile structural adhesive bonding. These developments, in particular much improved ability to bond oily/waxy surfaces common to the motor car industry and improved retention of fracture toughness after exposure to paint stoving temperatures, are discussed in this paper.     

Preparation, Characterisation and Catalytic Behaviour of a New TeVMoO Crystalline Phase

TeM_xMo_1.7O mixed oxides (M = V and/or Nb; x = 0-1.7) have been prepared by calcination of the corresponding salts at 600 °C in an atmosphere of N₂. A new crystalline phase, with a Te/V/Mo atomic ratio of 1/0.2-1.5/1.7, has been isolated and characterised by XRD and IR spectroscopy. This phase is observed in the TeVMo or TeVNbMo mixed oxide but not in the TeNbMo mixed oxide. The new crystalline phase shows an XRD pattern similar to Sb₄Mo₁₀O₃₁ and probably corresponds to the M1 phase recently proposed by Aouine et al. (Chem. Commun. 1180, 2001) to be present in the active and selective MoVTeNbO catalysts. Although these catalysts present a very low activity in the propane oxidation, they are active and selective in the oxidation of propene to acrolein and/or acrylic acid. However, the product distribution depends on the catalyst composition. Acrolein or acrylic acid can be selectively obtained from propene on Nb-free or Nb-containing TeVMo catalysts, respectively. The presence of both V and Nb, in addition to Mo and Te, appears to be important in the formation of acrylic acid from propene.     

Influence of the counter-ion on the effective charge of polyacrylic acid in dilute condition

Osmotic pressure measurements were satisfactorily used to compute the effective charge of poly(acrylic) acid (PAA) at different pHs and with different monovalent and divalent counterions. This experimental method is sensitive to the osmotically active species (polymer and counterions). After correction for the polymer contribution to the total osmotic pressure (solvency and excluded volume), the remaining pressure can be attributed to the polyelectrolyte counterions and processed with Donnan and equation of state in order to compute the effective charge number per polymeric chain (Z^eff). The behavior of Z^eff against the chain concentration and pH was investigated after neutralization of PAA with LiOH, NaOH, and TMAOH. The results clearly indicate that the nature of the monovalent counterion has no effect on Z^eff leading to the conclusion that the interaction between monovalent counterions and the acrylate functionality is purely electrostatic in agreement with conductimetric and potentiometric results reported in the literature. The behavior of Z^eff against the degree of ionization of the polymer and its concentration is also in good agreement with the theoretical expectations of the theory of ionic condensation. Osmotic measurements were also used in order to understand the influence of divalent cations (Mg²⁺, Ca²⁺, Ba²⁺) on Z^eff of the sodium salt of PAA at pH 9 and at different divalent/acrylate molar ratio. All the divalent cations depress Z^eff each of one at different degrees, confirming a specific divalent/polymer interaction. The energy of hydration of cations can explain most of the observed results with divalents.     

丙烯酸十六酯的合成及其降凝助滤效果

以丙烯酸和十六醇为原料,在丙烯酸/十六醇摩尔比为1.6,对甲苯磺酸质量分数为1.5%,对苯二酚质量分数为0.6%,反应温度为140℃,反应时间为5 h的条件下,制备了丙烯酸十六酯。结果表明,在上述最佳条件下,产物收率可达92%;在中国石油抚顺石化分公司石油一厂、二厂、三厂生产的0#柴油中,分别加入质量分数为0.5%的丙烯酸十六酯和T-1804降凝剂,前者的降凝助滤效果优于后者。