The structure,vacancy characteristics,and magnetic properties of GdMn1-xCrxO3 ceramics

To investigate the evolution of the structural and enhanced magnetic properties of GdMnO₃ systems induced by the substitution of Mn with Cr, polycrystalline GdMn_1-xCr_xO₃ samples were synthesized via solid-state reactions. XRD characterization shows that all GdMn_1-xCr_xO₃ compounds with single-phase structures crystallize well and that Cr³⁺ ions entering the lattice sites of GdMnO₃ induce structural distortion. SEM results indicate that the grain size of the synthesized samples (a few microns) decreases as the Cr substitution concentration increases. Positron annihilation lifetime spectroscopy reveals that vacancy-type defects occur in GdMn_1-xCr_xO₃ ceramics and that the vacancy size and concentration clearly change with the Cr content. The temperature and field dependence of the magnetization curves show that Cr substitution significantly influences the magnetic ordering of the gadolinium sublattice, improving the weak ferromagnetic transition temperature and magnetization of GdMn_1-xCr_xO₃. The enhanced magnetization of GdMn_1-xCr_xO₃ is closely related to the vacancy defect concentration.     

Interfacial microstructure and mechanical properties of Ti3SiC2 ceramic and TC11 alloy joint diffusion bonded with a Cu interlayer

Reliable joints of Ti₃SiC₂ ceramic and TC11 alloy were diffusion bonded with a 50 μm thick Cu interlayer. The typical interfacial structure of the diffusion boned joint, which was dependent on the interdiffusion and chemical reactions between Al, Si and Ti atoms from the base materials and Cu interlayer, was TC11/α-Ti + β-Ti + Ti₂Cu + TiCu/Ti₅Si₄ + TiSiCu/Cu(s, s)/Ti₃SiC₂. The influence of bonding temperature and time on the interfacial structure and mechanical properties of Ti₃SiC₂/Cu/TC11 joint was analyzed. With the increase of bonding temperature and time, the joint shear strength was gradually increased due to enhanced atomic diffusion. However, the thickness of Ti₅Si₄ and TiSiCu layers with high microhardness increased for a long holding time, resulting in the reduction of bonding strength. The maximum shear strength of 251 ± 6 MPa was obtained for the joint diffusion bonded at 850 °C for 60 min, and fracture primarily occurred at the diffusion layer adjacent to the Ti₃SiC₂ substrate. This work provided an economical and convenient solution for broadening the engineering application of Ti₃SiC₂ ceramic.     

Validation of scientific topic models using graph analysis and corpus metadata

Probabilistic topic modeling algorithms like Latent Dirichlet Allocation (LDA) have become powerful tools for the analysis of large collections of documents (such as papers, projects, or funding applications) in science, technology an innovation (STI) policy design and monitoring. However, selecting an appropriate and stable topic model for a specific application (by adjusting the hyperparameters of the algorithm) is not a trivial problem. Common validation metrics like coherence or perplexity, which are focused on the quality of topics, are not a good fit in applications where the quality of the document similarity relations inferred from the topic model is especially relevant. Relying on graph analysis techniques, the aim of our work is to state a new methodology for the selection of hyperparameters which is specifically oriented to optimize the similarity metrics emanating from the topic model. In order to do this, we propose two graph metrics: the first measures the variability of the similarity graphs that result from different runs of the algorithm for a fixed value of the hyperparameters, while the second metric measures the alignment between the graph derived from the LDA model and another obtained using metadata available for the corresponding corpus. Through experiments on various corpora related to STI, it is shown that the proposed metrics provide relevant indicators to select the number of topics and build persistent topic models that are consistent with the metadata. Their use, which can be extended to other topic models beyond LDA, could facilitate the systematic adoption of this kind of techniques in STI policy analysis and design.

     

Wall Rock Alteration,Uranium Mineralization,and Potentiality of Uranium and Iron Dissolution from Mineralized Abu Rusheid Gneiss Rock,South Eastern Desert,Egypt

Radiochemistry - Ferrugination, sericitization, desulfitization, chloritization, and kaolinitization of hydrothermal origin are the main wall rock alterations occurring within the NNW shear zones...     

Structural Aspects of P2-Type Na0.67Mn0.6Ni0.2Li0.2O2 (MNL) Stabilization by Lithium Defects as a Cathode Material for Sodium-Ion Batteries

A known strategy for improving the properties of layered oxide electrodes in sodium-ion batteries is the partial substitution of transition metals by Li. Herein, the role of Li as a defect and its impact on sodium storage in P2-Na_0.67Mn_0.6Ni_0.2Li_0.2O₂ is discussed. In tandem with electrochemical studies, the electronic and atomic structure are studied using solid-state NMR, operando XRD, and density functional theory (DFT). For the as-synthesized material, Li is located in comparable amounts within the sodium and the transition metal oxide (TMO) layers. Desodiation leads to a redistribution of Li ions within the crystal lattice. During charging, Li ions from the Na layer first migrate to the TMO layer before reversing their course at low Na contents. There is little change in the lattice parameters during charging/discharging, indicating stabilization of the P2 structure. This leads to a solid-solution type storage mechanism (sloping voltage profile) and hence excellent cycle life with a capacity of 110 mAh g^-1 after 100 cycles. In contrast, the Li-free compositions Na_0.67Mn_0.6Ni_0.4O₂ and Na_0.67Mn_0.8Ni_0.2O₂ show phase transitions and a stair-case voltage profile. The capacity is found to originate from mainly Ni³⁺/Ni⁴⁺ and O^2-/O^2-δ redox processes by DFT, although a small contribution from Mn⁴⁺/Mn⁵⁺ to the capacity cannot be excluded.     

Influence of SiC microstructure on its corrosion behavior in molten FLiNaK salt

The influence of the microstructure on the corrosion rate of three monolithic SiC samples in FLiNaK salt at 900 °C for 250 h was studied. The SiC samples, labeled as SiC-1, SiC-2, and SiC-3, had corrosion rates of 0.137, 0.020, and 0.043 mg/cm²h, respectively. Compared with grain size and the presence of special grain boundaries (i.e., Σ3), the content of high-angle grain boundaries (HAGBs) appeared to have the strongest influence on the corrosion rate of SiC in FLiNaK salt, since the corrosion rate increased six times as the concentration of high-angle grain boundaries increased from 19 to 32% for SiC-2 and SiC-1, respectively. These results stress the importance of controlling the content of HAGBs during the production process of SiC.     

A novel solution of deep learning for endoscopic ultrasound image segmentation: enhanced computer aided diagnosis of gastrointestinal stromal tumor

Multimedia Tools and Applications - Gastrointestinal stromal tumor is one of the critical tumors that doctors do not suggest to get frequent endoscopy, so there is a need for a diagnosis system...     

Corrosion behavior of T24, T92, VM12, and AISI 304 steels exposed to KCl–NaCl–K2SO4–Na2SO4 salt mixtures

The corrosion mechanisms of T24, T92, VM12, and AISI 304 steels are studied under the influence of NaCl–KCl, NaCl–Na₂SO₄, and KCl–K₂SO₄ salt mixtures in a dry air atmosphere at 650°C for 15 days. NaCl–KCl was the most aggressive deposit and AISI 304 stainless steel exhibited the highest corrosion resistance. There was no relation between the Cr content of the ferritic steels and their corrosion resistance in NaCl–KCl. In contrast, the resistance of high-Cr steels was better when exposed to NaCl–Na₂SO₄ and KCl–K₂SO₄. The high-Cr and the low-Cr steels were more susceptible to NaCl–Na₂SO₄ and to KCl–K₂SO₄, respectively.     

Amaranth functional cookies exert potential antithrombotic and antihypertensive activities

In this study, amaranth flour was used as an ingredient to prepare gluten-free cookies. The production process and attributes of amaranth cookies were characterised, and the potential use of amaranth flour as a functional ingredient was analysed. Cookies exhibited a non-uniform reddish brown colour and a cookie factor ratio of 4.5 ± 0.6. Storage studies indicated that after 3 weeks at room temperature cookies presented slight variations in the texture. Simulated gastrointestinal digestion of this product was able to release peptides capable of exerting potential antithrombotic and antihypertensive activities, IC₅₀ values of 0.22 ± 0.04 and 0.23 ± 0.03 mg mL⁻¹ protein, respectively. This work demonstrates for the first time that food made with amaranth flour exerts potential antithrombotic and antihypertensive activity. In conclusion, these amaranth cookies could be an alternative way of incorporating potentially health beneficial products for people who choose a conscious diet, including coeliac or vegan consumers.     

Iron(II) Sulfate(VI) from Titania Production as a Raw Material for Preparation of Hydrogen Sulfide Sorbents

A hybrid sorbent material for removal of hydrogen sulfide from air was developed. The material is based on activated carbon and iron compounds obtained from waste iron(II) sulfate(VI) heptahydrate. The iron salt is deposited on the carbonaceous support and subjected to oxidation (Fe²⁺ to Fe³⁺) using atmospheric oxygen under alkaline conditions. An effect of H₂O₂ addition to the process on the composition of the resultant material was also examined. X-ray diffraction (XRD) analyses confirmed easy conversion of waste FeSO₄·7H₂O to iron oxides Fe₃O₄ and FeOOH. The activated carbon supporting iron oxides revealed a higher efficiency in H₂S elimination from air compared to the commercial activated carbon, without any modification.