Transient liquid phase sintering of high-purity mullite for high-temperature structural ceramics

High-purity mullite ceramics, promising engineering ceramics for high-temperature applications, were fabricated using transient liquid phase sintering to improve their high-temperature mechanical properties. Small amounts of ultrafine alumina or silica powders were uniformly mixed with the mullite precursor depending on the silica-alumina ratio of the resulting ceramics to allow for the formation of a transient liquid phase during sintering, thus, enhancing densification at the early stage of sintering and mullite formation by the reaction between additional alumina and the residual glassy phase (mullitization) at the final stage of sintering. The addition of alumina powder to the silica-rich mullite precursor resulted in a reaction between the glassy silica and alumina phases during sintering, thereby forming a mullite phase without inhibiting densification. The addition of fine silica powder to the mullite single-phase precursor led to densification with an abnormal grain growth of mullite, whereas some of the added silica remained as a glassy phase after sintering. The resulting mullite ceramics prepared using different powder compositions showed different sintering behaviors, depending on the amount of alumina added. Upon selecting an optimum process and the amount of alumina to be added, the pure mullite ceramics obtained via transient liquid phase sintering exhibited high density (approximately 99%) and excellent high-temperature flexural strength (approximately 320 MPa) at 1500 °C in air. These results clearly demonstrate that pure mullite ceramics fabricated via transient liquid phase sintering with compositions close to those of stoichiometric mullite could be a promising process for the fabrication of high-temperature structural ceramics used in an ambient atmosphere. The transient liquid phase sintering process proposed in this study could be a powerful processing tool that allows for the preparation of superior high-temperature structural ceramics used in the ambient processing atmosphere.     

Dynamic probe of ZnTe(110) surface by scanning tunneling microscopy

The reconstructed surface structure of the II–VI semiconductor ZnTe (110), which is a promising material in the research field of semiconductor spintronics, was studied by scanning tunneling microscopy/spectroscopy (STM/STS). First, the surface states formed by reconstruction by the charge transfer of dangling bond electrons from cationic Zn to anionic Te atoms, which are similar to those of IV and III–V semiconductors, were confirmed in real space. Secondly, oscillation in tunneling current between binary states, which is considered to reflect a conformational change in the topmost Zn–Te structure between the reconstructed and bulk-like ideal structures, was directly observed by STM. Third, using the technique of charge injection, a surface atomic structure was successfully fabricated, suggesting the possibility of atomic-scale manipulation of this widely applicable surface of ZnTe.     

Distribution of carbon contamination in MgAl2O4 spinel occurring during spark-plasma-sintering (SPS) processing: I – Effect of heating rate and post-annealing

Carbon contamination from the carbon paper/dies during spark-plasma-sintering (SPS) processing was examined in the MgAl₂O₄ spinel. The carbon contamination sensitively changes with the heating rate during the SPS processing. At the high heating rate of 100 °C/min, the carbon contamination having organized structures occurred over almost the entire area from the surface to deep inside the SPSed spinel disk. In contrast, at the slow heating rate of 10 °C/min, the carbon contamination having disordered structures occurred only around the surface area. The carbon phases transform into high pressure CO/CO₂ gases by post-annealing in air and lead to pore formation along the grain junctions. The pore formation significantly occurs at the high heating rate due to the large amount of the contaminant carbon phases. This suggests that if once the carbon contamination was formed in the materials, it is very difficult to remove the carbon phases from the materials.     

Matrix influence on the piezoelectric properties of piezoelectric ceramic/polymer composite exhibiting particle alignment

This study was addressed to the influence of an electric field strength applied at fabrication process and matrix properties, such as the dielectric constant and the Young's modulus, on “pseudo‐1‐3 piezoelectric ceramic/polymer composite” in order to further enhance the piezoelectricity of that. The pseudo‐1‐3 piezoelectric ceramic/polymer composite consists of linearly ordered piezoelectric ceramic particles in polymer material. Silicone gel, silicone rubber, urethane rubber, and poly‐methyl‐methacrylate, which exhibit different dielectric constants and Young's modulus, were used as matrices to evaluate the matrix influence. The piezoelectricity of the pseudo‐1‐3 piezoelectric ceramic/polymer composite was evaluated using the piezoelectric strain constant d₃₃. The d₃₃ is one of the indices of the piezoelectric properties for piezoelectric materials. As a result, it was confirmed that d₃₃ of the pseudo‐1‐3 piezoelectric ceramic/polymer composite increased with the increase of the electric filed strength applied at fabrication process, though, it reached a constant value at a certain strength value. Further it was confirmed that dielectric constant of the matrix had a small influence on d₃₃ of the pseudo‐1‐3 piezoelectric ceramic/polymer composite, however, in case of matrix of lower Young's modulus, d₃₃ was increase. © 2014 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2015 , 132, 41817.     

Serum vanadium levels in chronic hemodialysis patients

Serum vanadium, aluminum, silicon and beta 2-microglobulin levels as well as the red cell count, hemoglobin and systolic blood pressure were simultaneously measured in 80 chronic hemodialysis patients. The serum vanadium level was positively correlated with the serum levels of aluminum, silicon and beta 2-microglobulin as well as the systolic blood pressure, and was inversely correlated with the red cell count and hemoglobin. The mean serum vanadium level was 18.4 +/- 7.6 ng/ml before hemodialysis and decreased to 13.0 +/- 5.30 ng/ml at the completion of dialysis. The dialysate vanadium level increased from 0.4 +/- 0.2 (inflow) to 1.0 +/- 0.4 ng/ml (outflow). It was concluded that vanadium was transferred from blood to dialysate when purified water was used in the preparation of the dialysate.     

Estramustine and estrone analogs rapidly and reversibly inhibit deoxyribonucleic acid synthesis and alter morphology in cultured human glioblastoma cells

Estramustine is an estradiol-based agent that has been shown to accumulate in human glioma cells, resulting in a concentration-dependent alteration in cell size and shape within minutes and an inhibition of proliferation over 3 to 6 days. We evaluated human glioblastoma cultures with [3H]thymidine incorporation assays to determine estramustine's early effects on deoxyribonucleic acid synthesis in these tumors. Because estramustine shares a common structural motif with other antimicrotubule drugs, we synthesized four A-ring conjugates of estrone that contained a carbamate moiety but lacked nitrogen mustard. These analogs were examined by [3H]thymidine incorporation and compared with vinblastine. Greater than 70% inhibition of [3H]thymidine incorporation occurred within 1 hour of treatment with estramustine at 10(-5) mol/L, which increased to 80% inhibition at 4 hours. Ethyl carbamate JE208 was nearly as effective as estramustine in inhibiting deoxyribonucleic acid synthesis, and both were more effective than vinblastine. The inhibitory effects of estramustine and estrone analogs were reversible; vinblastine was not reversible. Although estramustine and JE208 induced similar antiproliferative and morphological changes in glioblastoma cells that persisted for at least 4 days, there was a modest recovery of morphology and thymidine incorporation with JE208 after prolonged treatment. The common findings with estramustine and JE208 suggest that these agents may have a similar mechanism of action and form the basis for the investigation of new agents that may rapidly and reversibly inhibit glioblastoma.     

Effects of Neodymium Concentration on Optical Characteristics of Polycrystalline Nd:YAG Laser Materials

A neodymium-doped yttrium-aluminum garnet (Y₃A1₅O₁₂, YAG) (Nd:YAG) ceramic that contained 0.3–4.8 at.% neodymium additives and exhibited nearly the same optical properties as those of a single crystal was fabricated by a solid-state reaction method using high-purity powders. Although the integrated absorption intensity of the ²H_9/2+⁴F_5/2 bands simply increased as the neodymium concentration in the YAG ceramics decreased, the fluorescence intensity of the 2.4 at.% Nd:YAG ceramic was the strongest among Nd:YAG ceramics with various neodymium concentrations and a 0.9 at.% Nd:YAG single crystal. An oscillation experiment was performed on a continuous-wave (cw) laser with a diode-laser exciting system using those ceramics and the single crystal. The oscillation threshold and slope efficiency in that analysis were 309 mW and 28%, respectively, for the 1.1 at.% Nd:YAG ceramics and 356 mW and 40%, respectively, for the 2.4 at.% Nd:YAG ceramics. The lasing characteristics of the ceramics in the present work were superior to those of a 0.9 at.% Nd:YAG single crystal that was fabricated by the Czochralski (Cz) method.     

Characterization of localized states in thin PrBa2Cu3O7−x tunnel barriers

Characteristic power-law dependence of junction conductance on temperature was confirmed at low temperatures fora,b-axis oriented Au/PrBa₂Cu₃O_7−x /YBa₂Cu₃O_7−y junctions with a PrBa₂Cu₃O_7−x layer thinner than 30 nm, indicating that current transport via a small number of localized states was predominant. The radius and the density of the localized states were estimated to be 1.1 nm and 5.0x10¹⁹ eV⁻¹ cm⁻³, respectively. Transport measurement at 1.7 K in a magnetic field of up to 6 T revealed no indication of on-site Coulomb repulsion of electrons in the localized states. These results support the possibility of resonant tunneling of Cooper pairs in superconductor-insulator-superconductor junctions with a thin PrBa₂Cu₃O_7−x tunnel barrier.