A Study on the Standard Free Energy of Formation of LaNi_5 and CeNi_5

The temperature dependence of standard free energy of formation of LaNi_5,CeNi_5 has been de-termined by galvanic—cell technique using 0.95LaF_3·0.05CaF_2 polycrystalline solid electrolyte.The cellused can be expressed as:Mo|La,LaF_3|0.95LaF_3·0.05CaF2|LaNi_5,Ni,LaF_3|Mo(903～1173K)Mo|La|0.95LaF_3·0.05CaF_2|LaNi_5,Ni|Mo(903～1173K)Mo|Ce,CeF_3|0.95LaF_3·0.05CaF_2|CeNi_5,Ni,CeF_3|Mo(873～1023K)The experimental results are as follows:△G_(f,LaNi_5)~0=-152590+13.143T±150 J/mol(903～1173K)△G_(f,CeNi_5)~0=-157600+25.514T±150 J/mol(873～1023K)     

钙传感法对铁液中溶解态钙活度的研究

用直接合成法制备了Ｃａβ＂－Ａｌ２Ｏ３固体电解质，在１０＾－２～１ＭＨｚ频率范围内，于１０７３～１５２３Ｋ温度区间测定了电解质的阻抗谱，并计算得到电导率，其数量级为１０＾－６～１０＾－５Ω＾－１·ｃｍ＾－１。用Ｃａβ＂－Ａｌ２Ｏ３作为固体电解质，以Ｓｎ－Ｃａ合金为参比电极，组装成电池Ｍｏ｜Ｓｎ－Ｃａ｜Ｃａβ＂－Ａｌ２Ｏ３·｜［Ｃａ］Ｆｅ｜Ｍｏ（ＺｒＯ２），于１８３３Ｋ温度下测定了纯铁液中溶解态钙…     

富硼渣熔体物理性质测定

用化学试剂氧化物配制合成富硼渣，利用ＺＣ－１６００型高温综合测试仪、内柱体旋转法测定其粘度及熔化性温度；双柱联称法同时测定熔渣的密度及表面张力。探讨了富硼渣组成与熔体物理性质的关系，为优化硼铁矿高炉铁硼分离工艺提供依据。     

用铬传感器测定碳饱和铁液中的Cr的活度

用ＺｒＯ２（ＭｇＯ）固体电解质，以ＣａＳｉＯ３＋Ｃｒ２Ｏ３作为辅助电极，组成铬传感探头：ＭｏＣｒ，Ｃｒ２Ｏ３，ＺｒＯ２（ＭｇＯ）ＣａＳｉＯ３，Ｃｒ２Ｏ３Ｃｒ）ＦｅＭｏ－ＺｒＯ２于１７５３Ｋ测定了碳饱和铁液中Ｃｒ的活度，该探头响应快，约２－３ｓ即可得到稳定的电动势值，测定误差为±１－２ｍＶ，Ｃｒ的活度与Ｃｒ的浓度之间符合理论关系。     

B_2O_3－MgO－SiO_2－Al_2O_3－CaO系渣组成对熔体物性的影响

用柱体旋转法测定了Ｂ_２Ｏ_３—ＭｇＯ—ＳｉＯ_２—Ａｌ２Ｏ_３—ＣａＯ系富硼镁渣的粘度及熔化性温度，用双柱联称法测定熔渣的密度及表面张力．实验结果表明：富硼镁渣的粘度及熔化性温度随渣中Ｂ_２Ｏ_３含量的增加而降低；当Ｂ_２Ｏ_３含量一定时，随渣中ＭｇＯ量及渣碱度的增加而增大．熔体的密度及表面张力随ＭｇＯ量增加或ＳｉＯ_２量减少而增大，分别为（２．５±０．５）ｔ·ｍ~（－３）和０．４－０．６Ｎ·ｍ~（－１）．     

用铬传感器测定碳饱和铁液中Cr的活度

用ZrO2（MgO）固体电解质，以CasiO3＋Cr2O3作为辅助电极，组成铬传感探头：Mo|Cr，Cr2O3|ZrO2（MgO）|CaSiO3，Cr2O3|[Cr]Fe|Mo－ZrO2于1753K测定了碳饱和铁液中Cr的活度该探头响应快，约2—3s即可得到稳定的电动势值，测定误差为主±1～2mVCr的活度与Cr的浓度之间符合理论关系     

Ion Exchange Reaction between Polycrystalline Na β″-Alumina and LaCl_3

1.IntroductionDunn and Farrington[1]found that theNa ion in Naβ″-alumina single crystal canbe exchanged completely or partially withGd~(3+),Nd~(3+),Eu~(3+),Yb~(3+),Sm~(3+),Tb~(3+),Dy~(3+),Bi~(3+)and Pr~(3+)ions,but no reports havebeen published about the ion exchange reac-tion between La3+ and Naβ″-alumina.If anion exchanged polycrystalline β″-alumina isavailable and its ionic conductivity is highenough to be applied as a solid electrolyte inthe galvanic cell,it can be used in various     

B2O3—MgO—SiO2—Al2O3—CaO系渣组成对溶体物性的影响

用柱体旋转法测定了Ｂ_２Ｏ_３—ＭｇＯ—ＳｉＯ_２—Ａｌ２Ｏ_３—ＣａＯ系富硼镁渣的粘度及熔化性温度，用双柱联称法测定熔渣的密度及表面张力．实验结果表明：富硼镁渣的粘度及熔化性温度随渣中Ｂ_２Ｏ_３含量的增加而降低；当Ｂ_２Ｏ_３含量一定时，随渣中ＭｇＯ量及渣碱度的增加而增大．熔体的密度及表面张力随ＭｇＯ量增加或ＳｉＯ_２量减少而增大，分别为（２．５±０．５）ｔ·ｍ~（－３）和０．４－０．６Ｎ·ｍ~（－１）．     

Gibbs Free Energy of Formation of 3Y_2O_3·5Al_2O_3

Thermodynamic properties of 3Y_2O_3·5Al_2O_3 double compound have been determined with CaF_2 single crystal electrolyte galvanic cell at 1049 K to 1230 K.The galvanic cell used can be expressed as: Pt,O_2(g)丨Y_2O_3(s),YOF_((s))丨CaF_2丨YOF_((s)), 3Y_2O_3·5Al_2O_(3(s))丨Al_2O_(3(s))丨O_2(g),Pt, of which the cell reaction is; 3Y_2O_(3(s))+SAl_2O_(3(s))=3Y_2O_3·SAl_2O_(3(s)) The following result is obtained: A_fG°(3Y_2O_3·5Al_2O_3)=-939500+765.90T±710J/mol where,△fG°(3Y_2O_3·5Al_2O_3)is the free energy of formation of 3Y_2O_3·5Al_2O_3 from Y_2O_3 and Al_2O_3.     

B_2O_3－MgO－SiO_2－Al_2O_3－CaO熔渣的密度及表面张力

为综合利用开发硼铁矿资源，模拟硼铁矿高温选择性还原－熔融分离铁硼工艺的渣组成，用化学试剂合成配制Ｂ２Ｏ３－ＭｇＯ－ＳｉＯ２－Ａｌ２Ｏ３－ＣａＯ渣样，在ＺＣ－１６００型高温综合测试仪上，用双柱联称法同时测定熔渣的密度及表面张力。结果表明：在１４６０～１５００℃密度为２．５±０．５ｇ·ｃｍ－３表面张力为０．４～０．６Ｎ·ｍ－１。其密度及表面张力均随渣中ＭｇＯ含量的增加，或随ＳｉＯ２量的减少而增大，随温度的提高而变小。